11 resultados para soil dissolved C pool
em Cambridge University Engineering Department Publications Database
Resumo:
Soil-mix technology is effective for the construction of permeable reactive barriers (PRBs) for in situ groundwater treatment. The objective of this study was to perform initial experiments for the design of soil-mix technology PRBs according to (i) sorption isotherm, (ii) reaction kinetics and (iii) mass balance of the contaminants. The four tested reactive systems were: (i) a granular zeolite (clinoptilolite-GZ), (ii) a granular organoclay (GO), (iii) a 1:1-mixture GZ and model sandy clayey soil and (iv) a 1:1:1-mixture of GZ, GO and model soil. The laboratory experiments consisted of batch tests (volume 900mL and sorbent mass 18g) with a multimetal solution of Pb, Cu, Zn, Cd and Ni. For the adsorption experiment, the initial concentrations ranged from 0.01 to 0.5mM (2.5 to 30mg/L). The maximum metal retention was measured in a batch test (300mg/L for each metal, volume 900mL, sorbent mass 90-4.5g). The reactive material efficiency order was found to be GZ>GZ-soil mix>GZ-soil-GO mix>GO. Langmuir isotherms modelled the adsorption, even in presence of a mixed cations solution. Adsorption was energetically favourable and spontaneous in all cases. Metals were removed according to the second order reaction kinetics; GZ and the 1:1-mix were very similar. The maximum retention capacity was 0.1-0.2mmol/g for Pb in the presence of clinoptilolite; for Cu, Zn, Cd and Ni, it was below 0.05mmol/g for the four reactive systems. Mixing granular zeolite, organoclay and model soil increased the chemisorption. Providing that GZ is reactive enough for the specific conditions, GZ can be mixed to obtain the required sorption. Granular clinoptilolite addition to soil is recommended for PRBs for metal contaminated groundwater. The laboratory experiments consisted of batch tests with a multimetal solution of Pb, Cu, Zn, Cd and Ni. The four reactive materials chosen were granular zeolite, clinoptilolite and model sandy clayey soil, granular organoclay and a mix of clinoptilolite, model soil and organoclay. The reactive material efficiency order was found to be granular clinoptilolite>clinoptilolite-soil mix>clinoptilolite-soil-organoclay mix>granular organoclay. © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Resumo:
This paper presents details of the installation and performance of carbonated soil-MgO columns using a laboratory-scale model auger setup. MgO grout was mixed with the soil using the auger and the columns were then carbonated with gaseous CO2 introduced in two different ways: one using auger mixing and the other through a perforated plastic tube system inserted into the treated column. The performance of the columns in terms of unconfined compressive strength (UCS), stiffness, strain at failure and microstructure (using X-ray diffraction and scanning electron microscopy) showed that the soil-MgO columns were carbonated very quickly (in under 1 h) and yielded relatively high strength values, of 2.4-9.4 MPa, which on average were five times that of corresponding 28-day ambient cured uncarbonated columns. This confirmed, together with observations of dense microstructure and hydrated magnesium carbonates, that a good degree of carbonation had taken place. The results also showed that the carbonation method and period have a significant effect on the resulting performance, with the carbonation through the perforated pipe producing the best results. Copyright © 2013 by ASTM International.
Resumo:
This paper investigates the potential for carbonating reactive magnesia (MgO) to serve as a more sustainable soil stabilization method by providing rapid and significant strength development of the stabilized soil through absorbing substantial quantities of CO2. Gaseous CO2 was forced through laboratory-prepared reactive MgO-treated soil samples in a triaxial cell set-up, and their resulting mechanical and microstructural properties were investigated using unconfined compressive strength, X-ray diffraction, and scanning electron microscopy. The results showed that adequately carbonated MgO-treated soils could, in a few hours, reach a similar strength range to corresponding 28 day Portland cement (PC)-stabilized soils. Hydrated magnesium carbonates, namely nesquehonite and hydromagnesite-dypingite, were the main products of the carbonated MgO in the soil, and were responsible for the significant strength development.
Resumo:
Relatively new in the UK, soil mix technology applied to the in-situ remediation of contaminated land involves the use of mixing tools and additives to construct permeable reactive in-ground barriers and low-permeability containment walls and for hot-spot soil treatment by stabilisation/ solidification. It is a cost effective and versatile approach with numerous environmental advantages. Further commercial advantages can be realised by combining this with ground improvement through the development of a single integrated soil mix technology system which is the core objective of Project SMiRT (Soil Mix Remediation Technology). This is a large UK-based R&D project involving academia-industry collaboration with a number of tasks including equipment development, laboratory treatability studies, field trials, stakeholder consultation and dissemination activities. This paper presents aspects of project SMiRT relating to the laboratory treatability study work leading to the design of the field trials. © 2012 American Society of Civil Engineers.