Effect of size, morphology and crystallinity of seed crystal on the nucleation and growth of single grain Y-Ba-Cu-O

The effect of size, morphology and crystallinity of seed crystals on the nucleation and growth of large grain Y-Ba-Cu-O (YBCO) bulk superconductors fabricated by top seeded melt growth (TSMG) has been investigated. Seeding bulk samples with small, square shaped seed crystals leads to point nucleation and growth of the superconducting YBa2Cu3O7-y (Y-123) phase that exhibits the usual square habitual growth symmetry. The use of triangular and circular shaped seed crystals, however, modifies significantly the growth habit geometry of the grain. The use of large area seeds both increases the rate of epitaxial nucleation of the Y-123 phase and produces relatively large crystals in the incongruent melt, which decreases significantly the processing times of large grain samples. The present study is relevant to decrease processing times of samples with both preferred or no growth sectors and for multiple seeding of large grain samples which contain clean grain boundaries. © 2005 Published by Elsevier Ltd.

Single domain YBCO/Ag bulk superconductors fabricated by seeded infiltration and growth

We have applied the seeded infiltration and growth (IG) technique to the processing of samples containing Ag in an attempt to fabricate Ag-doped Y-Ba-Cu-O (YBCO) bulk superconductors with enhanced mechanical properties. The IG technique has been used successfully to grow bulk Ag-doped YBCO superconductors of up to 25 mm in diameter in the form of single grains. The distribution of Ag in the parent Y-123 matrix fabricated by the IG technique is observed to be at least as uniform as that in samples grown by conventional top seeded melt growth (TSMG). Fine Y-211 particles were observed to be embedded within the Y-123 matrix for the IG processed samples, leading to a high critical current density, Jc, of over 70 kA/cm2 at 77.3 K in self-field. The distribution of Y-211 in the IG sample microstructure, however, is inhomogeneous, which leads to a variation in the spatial distribution of Jc throughout the bulk matrix. A maximum-trapped field of around 0.43 T at 1.2 mm above the sample surface (i.e. including 0.7 mm for the sensor mould thickness) is observed at liquid nitrogen temperature, despite the relatively small grain size of the sample (20 mm diameter × 7 mm thickness). © 2008 IOP Publishing Ltd.