ROLE OF CHLORINE AND ALKALI PROMOTERS IN ETHYLENE EPOXIDATION OVER SINGLE CRYSTAL SILVER SURFACES.

Experiments with N//2O were carried out with a view to obtaining additional information about the reactivity of oxygen surface species. On clean Ag, N//2O decomposition was found to be an activated process which led exclusively to the deposition of O(a) species. The presence of preadsorbed oxygen or subsurface oxygen served to enhance the deposition rate of O(a). Subsequent dosing with ethylene at 300 K of such an oxygen-populated surface followed by TPR examination showed it to be active for ethylene oxide formation. Control experiments established that adventitious decomposition of N//2O at the reactor walls or specimen supports followed by possible re-absorption of O//2(a) was an entirely negligible process. ) The oxidation activity of N//2O was also investigated at elevated pressures in the batch reactor.

Mechanism And Selectivity In The Epoxidation Of Ethylene Over Silver: The Results Of Single Crystal Measurements

The silver-catalysed oxidation of ethylene has been examined on the (III) face of a single crystal by a combination of electron spectroscopy and kinetic measurements at pressures of up to 50 Torr. The necessary and sufficient conditions for ethylene oxide formation are established, reaction intermediates are identified, kinetic isotope effects are observed and the role of Cs in modifying reaction selectivity is examined. It is shown that surface alkali exhibits opposite effects on the reactions which lead to the further oxidation of ethylene oxide and on the direct combustion of ethylene. © 1984.

SiO2 coating of silver nanoparticles by photoinduced chemical vapor deposition.

Gas-phase silver nanoparticles were coated with silicon dioxide (SiO2) by photoinduced chemical vapor deposition (photo-CVD). Silver nanoparticles, produced by inert gas condensation, and a SiO2 precursor, tetraethylorthosilicate (TEOS), were exposed to vacuum ultraviolet (VUV) radiation at atmospheric pressure and varying temperatures. The VUV photons dissociate the TEOS precursor, initiating a chemical reaction that forms SiO2 coatings on the particle surfaces. Coating thicknesses were measured for a variety of operation parameters using tandem differential mobility analysis and transmission electron microscopy. The chemical composition of the particle coatings was analyzed using energy dispersive x-ray spectrometry and Fourier transform infrared spectroscopy. The highest purity films were produced at 300-400 degrees C with low flow rates of additional oxygen. The photo-CVD coating technique was shown to effectively coat nanoparticles and limit core particle agglomeration at concentrations up to 10(7) particles cm(-3).