The effects of corona treatment on impact and spreading of ink-jet drops on a polymeric film substrate

The effects of varying corona surface treatment on ink drop impact and spreading on a polymer substrate have been investigated. The surface energy of substrates treated with different levels of corona was determined from static contact angle measurement by the Owens and Wendt method. A drop-on-demand print-head was used to eject 38 μm diameter drops of UV-curable graphics ink travelling at 2.7 m/s on to a flat polymer substrate. The kinematic impact phase was imaged with a high speed camera at 500k frames per second, while the spreading phase was imaged at 20k frames per secoiui. The resultant images were analyzed to track the changes in the drop diameter during the different phases of drop spreading. Further experiments were carried out with white-light intetferometry to accurately measure the final diameter of drops which had been printed on different corona treated substrates and UV cured. The results are correlated to characterize the effects of corona treatment on drop impact behavior and final print quality.

Cold-gas chemical vapor deposition to identify the key precursor for rapidly growing vertically-aligned single-wall and few-wall carbon nanotubes from pyrolyzed ethanol

Vertically-aligned carbon nanotubes (VA-CNTs) were rapidly grown from ethanol and their chemistry has been studied using a "cold-gas" chemical vapor deposition (CVD) method. Ethanol vapor was preheated in a furnace, cooled down and then flowed over cobalt catalysts upon ribbon-shaped substrates at 800 °C, while keeping the gas unheated. CNTs were obtained from ethanol on a sub-micrometer scale without preheating, but on a millimeter scale with preheating at 1000 °C. Acetylene was predicted to be the direct precursor by gas chromatography and gas-phase kinetic simulation, and actually led to millimeter-tall VA-CNTs without preheating when fed with hydrogen and water. There was, however a difference in CNT structure, i.e. mainly few-wall tubes from pyrolyzed ethanol and mainly single-wall tubes for unheated acetylene, and the by-products from ethanol pyrolysis possibly caused this difference. The "cold-gas" CVD, in which the gas-phase and catalytic reactions are separately controlled, allowed us to further understand CNT growth. © 2012 Elsevier Ltd. All rights reserved.

Spray drying: An alternative synthesis method for polycationic oxide compounds

Synthesis of polycationic compounds by the spray-drying technique is an interesting alternative in the domain of aqueous precursor synthesis methods. Spray drying yields high quality samples with good reproducibility. The possibility of scaling up for production of large quantities with fast processing time is well established by the commercial availability of powders of various compositions. In this paper, we have discussed the advantages and limitations of this method and demonstrated its interest by synthesizing a few polycationic compounds selected for their attractive properties of thermoelectricity [Bi1.68Ca2Co1.69O 8, La0.95A0.05CoO3 (A=Ca, Sr, Ba)] or magnetoresistance [La0.70A0.30MnO3 (A=Sr, Ba)]. We have confirmed the quality of these samples by reporting their structure, magnetic and transport properties. © 2010 Elsevier Ltd All rights reserved.