The effect of addition of ZrO2 to Fe2O3 for hydrogen production by chemical looping

In this paper, a synthetic mixture of ZrO2 and Fe 2O3 was prepared by coprecipitation for use in chemical looping and hydrogen production. Cycling experiments in a fluidized bed showed that a material composed of 30 mol % ZrO2 and 70 mol % Fe 2O3 was capable of producing hydrogen with a consistent yield of 90 mol % of the stoichiometric amount over 20 cycles of reduction and oxidation at 1123 K. Here, the iron oxide was subjected to cycles consisting of nearly 100% reduction to Fe followed by reoxidation (with steam or CO 2 and then air) to Fe2O3. There was no contamination by CO of the hydrogen produced, at a lower detection limit of 500 ppm, when the conversion of Fe3O4 to Fe was kept below 90 mol %. A preliminary investigation of the reaction kinetics confirmed that the ZrO2 support does not inhibit rates of reaction compared with those observed with iron oxide alone. © 2012 American Chemical Society.

Carrier lifetime and mobility enhancement in nearly defect-free core-shell nanowires measured using time-resolved terahertz spectroscopy.

We have used transient terahertz photoconductivity measurements to assess the efficacy of two-temperature growth and core-shell encapsulation techniques on the electronic properties of GaAs nanowires. We demonstrate that two-temperature growth of the GaAs core leads to an almost doubling in charge-carrier mobility and a tripling of carrier lifetime. In addition, overcoating the GaAs core with a larger-bandgap material is shown to reduce the density of surface traps by 82%, thereby enhancing the charge conductivity.

Nearly intrinsic exciton lifetimes in single twin-free GaAsAlGaAs core-shell nanowire heterostructures

CW and time-resolved photoluminescence measurements are used to investigate exciton recombination dynamics in GaAsAlGaAs heterostructure nanowires grown with a recently developed technique which minimizes twinning. A thin capping layer is deposited to eliminate the possibility of oxidation of the AlGaAs shell as a source of oxygen defects in the GaAs core. We observe exciton lifetimes of ∼1 ns, comparable to high quality two-dimensional double heterostructures. These GaAs nanowires allow one to observe state filling and many-body effects resulting from the increased carrier densities accessible with pulsed laser excitation. © 2008 American Institute of Physics.