Increasing the life of flare tips

Flare tips are essential for safety. Maintenance is difficult and costly. Flare tips are subjected to high combustion temperatures, thermal cycling, oxidation and marine corrosion. Following a number of flare tip failures an in depth study by Imperial College was carried out into the failure of a flare tip from a UK platform, looking for service life improvement. Materials selection and design solutions were considered. The study considered alternative materials and concluded that materials selection was the smaller part of the answer; design changes can double service life. This study used failure investigation, high temperature experimental and thermo-mechanical modelling analysis. The modelling process simulated two common flaring conditions and correctly predicted the observed failure of initiation and crack propagation from holes used to bolt on flame stabilizing plates to the top of the flare. The calculated thermal stress and strains enabled the low cycle fatigue life and minimum creep life to be predicted. It was concluded that service life could be improved by replacing Incoloy alloy 800HT (UNS N08800) with Inconel alloy 625 (UNS N06625), an alloy with attractive mechanical properties and improved high temperature corrosion resistance. Repositioning or eliminating bolt holes can double service life. Copyright 2008, Society of Petroleum Engineers.

Thermal shock resistance of air plasma sprayed thermal barrier coatings

The spallation resistance of an air plasma sprayed (APS) thermal barrier coating (TBC) to cool-down/reheat is evaluated for a pre-existing delamination crack. The delamination emanates from a vertical crack through the coating and resides at the interface between coating and underlying thermally grown oxide layer (TGO). The coating progressively sinters during engine operation, and this leads to a depth-dependent increase in modulus. Following high temperature exposure, the coating is subjected to a cooling/reheating cycle representative of engine shut-down and start-up. The interfacial stress intensity factors are calculated for the delamination crack over this thermal cycle and are compared with the mode-dependent fracture toughness of the interface between sintered APS and TGO. The study reveals the role played by microstructural evolution during sintering in dictating the spallation life of the thermal barrier coating, and also describes a test method for the measurement of delamination toughness of a thin coating. © 2014 Elsevier Ltd.