Critical current densities of MOCVD tapes for different current directions

The critical current density Jc of an MOCVD/IBAD coated conductor was measured on tracks patterned longitudinally (L) and transversely (T) to the tape direction. Despite the samples' vicinality no dependence J c of on track direction was found for magnetic fields applied perpendicular to the film plane. In angular out-of-plane measurements the previously reported asymmetry due to tilted precipitate planes was observed in an L track, whereas curves from a T track were almost perfectly symmetric with similarly high absolute values of Jc. At low fields the effects of surface pinning were seen. Our results show that in most scenarios the current carrying capability is equally as good parallel and perpendicular to the tape direction, which is highly relevant for ROEBEL cables. In measurements where the magnetic field was swept in the film plane the anisotropy was found to be significantly higher than for MOD/RABiTS samples, which we explain by the different morphology of grain boundaries in the tapes. At low temperatures Jc of a T track exhibited a clear signature of vortex channeling. © 2010 IEEE.

Alternating current loss of second-generation high-temperature superconducting coils with magnetic and non-magnetic substrate

It is widely believed that the second-generation high-temperature superconducting (2G HTS) tapes with magnetic substrates suffer higher transport loss compared to those with non-magnetic substrates. To test this, we prepared two identical coils with magnetic and non-magnetic substrates, respectively. The experimental result was rather surprising that they generated roughly the same amount of transport loss. We used finite element method to understand this result. It is found that, unlike in the single tape where the magnetic field-dependent critical current characteristic can be neglected and the effect of magnetic substrate dominates, the magnetic field-dependent critical current characteristic of 2G tape plays as an equally important role as magnetic substrate in terms of HTS coils. © 2012 American Institute of Physics.

Identification of support conditions of buried pipes using a vibrating pig

This paper describes a method for monitoring the variation in support condition of pipelines using a vibration technique. The method is useful for detecting poor support of buried pipelines and for detecting spanning and depth of cover in sub-sea lines. Variation in the pipe support condition leads to increased likelihood of pipe damage. Under roadways, poorly supported pipe may be damaged by vehicle loading. At sea, spanned sections of pipe are vulnerable to ocean current loading and also to snagging by stray anchors in shallow waters. A vibrating `pig' has been developed and tested on buried pipelines. Certain features of pipe support, such as voids and hard spots, display characteristic responses to vibration, and these are measured by the vibrating pig. Post-processing of the measured vibration data is used to produce a graphical representation of the pipeline support and certain `feature characteristics' are identified. In field tests on a pipeline with deliberately constructed support faults, features detected by the vibrating pig are in good agreement with the known construction.

Distribution of critical current density in large YBa2Cu3O7-δ grains fabricated using seeded peritectic solidification

High quality large grain high Tc superconducting ceramics offer enormous potential as 'permanent' magnets and in magnetic screening applications at 77K. This requires sample dimensions -cm with uniform high critical current densities of the order 105 A/cm2 in applied magnetic fields of IT. We report a study of the magnetic characterisation of a typical large YBa2Cu3O7-δ grain, prepared by seeded peritectic solidification, and correlate the magnetically determined critical current density, Jc, with microstuctural features from different regions of the bulk sample. From this data we extract the temperature, field and positional dependence of the critical current density of the samples and the irreversibility line. We find that whilst the bulk sample exhibits a good Jc of order 104 A/cm2 (77K, 1T), the local Jc is strongly correlated with the sample microstructure towards the edge of the sample and more severely at the centre of the sample by the presence of SmBa2Cu3O7-δ seed crystal. © 1997 IEEE.