Comparative study of the slurry erosion and free-fall particle erosion of aluminum

A study has been performed of the erosion of aluminium by silica sand particles at a velocity of 4.5 m s-1, both air-borne and in the form of a water-borne slurry. Measurements made under similar experimental conditions show that slurry erosion proceeds at a rate several times that of air-borne erosion, the ratio of the two rates depending strongly on the angle of impact. Sand particles become embedded into the metal surface during air-borne particle erosion, forming a composite layer of metal and silica, and provide the major cause of the difference in wear rate. The embedded particles giving rise to surface hardening and a significant reduction in the erosion rate. Embedment of erodent particles was not observed during slurry erosion. Lubrication of the impacting interfaces by water appears to have minimal effect on the wear of aluminium by slurry erosion.

Resistance of cast polyurethane elastomers to solid particle erosion

The rates of erosive wear have been measured for a series of eight polyester-based one-component castable polyurethane elastomers, with widely varying mechanical properties. Erosion tests were conducted with airborne silica sand, 120μm in particle size, at an impact velocity of 50 ms-1 and impact angles of 30° and 90°. For these materials, which all showed similar values of rebound resilience, the erosion rate increased with increasing hardness, tensile modulus and tensile strength. These findings are at variance with those expected for wear by abrasion, perhaps because of differences in the strain rate or strain levels imposed on the elastomer during erosion and abrasion.

Comparison between weight loss of bends in a pneumatic conveyor and erosion rate obtained in a centrifugal erosion tester for the same materials

In order to find a link between results obtained from a laboratory erosion tester and tests carried out on a pneumatic conveyor, a comparison has been made between weight loss from bends on an industrial-scale pneumatic conveyor and erosion rates obtained in a small centrifugal erosion tester, for the same materials. Identical test conditions have been applied to both experiments so that comparable test results have been obtained. The erosion rate of mild steel commonly used as the wall material of conveyor pipes and pipe bends was determined individually on both test rigs. A relationship between weight loss from the bends and erosion rate determined from the tester has been developed. A discussion based on the results and their applicability to the prediction of wear in pneumatic conveyors concludes the paper. © 2004 Elsevier B.V. All rights reserved.

Coatings and surface treatments for protection against low-velocity erosion-corrosion in fluidized beds

Surface coatings and treatments have been used to reduce material loss of components in bubbling fluidized bed combustors (FBCs). The performance of protective coatings in FBC boilers and laboratory simulations is reviewed. Important coating properties to minimize wastage appear to be high hardness, low oxidation rate, low porosity, high adhesion and sufficient thickness to maintain protection for a long period. Economic considerations and criteria for choosing a suitable coating or treatment are discussed for the different types of bubbling FBC. © 1995.