Selective epitaxial growth in silicon on insulator: Planarity and mass flow

Seeded zone-melt recrystallization using a dual electron beam system has been performed on silicon-on-insulator material, which was prepared with single-crystal silicon filling of the seed windows by selective epitaxial growth. The crystal quality has been assessed by a variety of microscopic techniques, and it is shown that single-crystal films 0.5-1.0 μm thick over 1.0 μm of isolating oxide may be prepared by this method. These films have considerably less lateral variation in thickness than standard material, in which the windows are not so filled. The filling method is suitable for both single- and multiple-layer silicon-on-insulator, and gives the advantages of excellent layer uniformity after recrystallization and improved planarity of the whole chip structure. Experiments using various amounts of seed window filling have shown that the lateral variations of silicon film thickness seen in unplanarized material are due to stress relief in the cap oxide when the silicon film is molten, rather than the effect previously postulated in which they were assumed to be due to the contraction of silicon on melting.

A simple combinatorial method aiding research on single-walled carbon nanotube growth on substrates

Establishing fabrication methods of carbon nanotubes (CNTs) is essential to realize many applications expected for CNTs. Catalytic growth of CNTs on substrates by chemical vapor deposition (CVD) is promising for direct fabrication of CNT devices, and catalyst nanoparticles play a crucial role in such growth. We have developed a simple method called "combinatorial masked deposition (CMD)", in which catalyst particles of a given series of sizes and compositions are formed on a single substrate by annealing gradient catalyst layers formed by sputtering through a mask. CMD enables preparation of hundreds of catalysts on a wafer, growth of single-walled CNTs (SWCNTs), and evaluation of SWCNT diameter distributions by automated Raman mapping in a single day. CMD helps determinations of the CVD and catalyst windows realizing millimeter-tall SWCNT forest growth in 10 min, and of growth curves for a series of catalysts in a single measurement when combined with realtime monitoring. A catalyst library prepared using CMD yields various CNTs, ranging from individuals, networks, spikes, and to forests of both SWCNTs and multi-walled CNTs, and thus can be used to efficiently evaluate self-organized CNT field emitters, for example. The CMD method is simple yet effective for research of CNT growth methods. © 2010 The Japan Society of Applied Physics.