Analysis of asphalt concrete permeability data using representative pore size

The permeability of asphalt concrete has been the subject of much study by pavement engineers over the last decade. The work undertaken has tended to focus on high air voids as the primary indicator of permeable asphalt concrete. This paper presents a simple approach for understanding the parameters that affect permeability. Principles explained by Taylor in 1956 in channel theory work for soils are used to derive a new parameter-representative pore size. Representative pore size is related to the air voids in the compacted mix and the D75 of the asphalt mix grading curve. Collected Superpave permeability data from published literature and data collected by the writers at the Queensland Department of Transport and Main Roads is shown to be better correlated with representative pore size than air voids, reducing the scatter considerably. Using the database of collected field and laboratory permeability values an equation is proposed that pavement engineers can use to estimate the permeability of in-place pavements. © 2011 ASCE.

Fracture mechanics of idealised bituminous mixes

© 2014 Taylor & Francis. The durability of asphalt pavements is strongly impaired by cracks, caused primarily by traffic loads and environmental effects. In this work, fracture behaviour of idealised asphalt mixes is investigated. Experiments on idealised asphalt mixes under pure-tension mode (mode I cracking) were performed and fracture parameters were evaluated. In these three-point bend fracture tests, the test variables were temperature and load rate. The test data were stored in an asphalt materials database and special-purpose tools were implemented to analyse and handle the laboratory data automatically. Fracture mechanism maps were constructed, showing the conditions associated with ductile, brittle and ductile-brittle transition regimes of behaviour. The mechanism maps show the failure response of the material in terms of the stress intensity factor, strain energy release rate and J-integral as a function of the temperature-compensated crack mouth opening strain rate. Fracture behaviour of asphalt mix specimens was simulated by cohesive zone model in conjunction with a novel material constitutive model for asphalt mixes. The finite element model agrees well with the experimental results and provides insights into fracture response of the notched asphalt mix beam specimens.