Increasing the design strength of glass – fractography and stress testing

Brittleness is the unintended, but inevitable consequence of producing a transparent ceramic for architectural applications such as the soda-lime glass. Its tensile strength is particularly sensitive to surface imperfections, such as that from natural weathering and malicious damage. Although a significant amount of testing of new glass has been carried out, there has been surprisingly little testing on weathered glass. Due to the variable nature of the causes of surface damage, the lack of data on weathered glass leads to a considerable degree of uncertainty in the long-term strength of exposed glass. This paper presents the results of recent tests on weathered annealed glass which has been exposed to natural weathering for more than 20 years. The tests include experimental investigations using the co-axial ring setup as well as optical and atomic force microscopy of the glass surfaces. The experimental data from these tests is subsequently used to extend existing fracture mechanics-based models to predict the strength of weathered glass. It is shown that using an automated approach based directly on finite element analysis results can give an increase in effective design strength in the order of 70 to 100% when compared to maximum stress methods. It is also shown that by combining microscopy and strength test results, it is possible to quantitatively characterise the damage on glass surfaces.

Influence of Peripheral Velocity on Vane Shear Strength of an Artificial Clay

Shearing rate is among the most important factors affecting the undrained shear strength of clays. In particular, for seismic or storm-wave loading conditions, the shearing rate is much higher than that used in many common laboratory or field tests. The testing program described here evaluates the effect of peripheral velocity on the undrained strength inferred from the shear vane test. The study was conducted on a lightly cemented bentonite-kaolinite mixture manufactured in the laboratory, which possesses many characteristics similar to those of natural materials. Results show that the shear strength increases with increasing peripheral velocity, while the residual shear strength seems to be nearly independent of rotation rate.