Hermetically-coated superparamagnetic Fe2O3 particles with SiO2 nanofilms

Magnetic nanoparticles are frequently coated with SiO2to improve their functionality and bio-compatibility in a range of biomedical and polymer nanocomposile applications. In this paper, a scalable flame aerosol technology is used to produce highly dispersible, superparamagnetic iron oxide nanoparticles hermetically coaled with silica to retain full magnetization performance. Iron oxide particles were produced by flame spray pyrolysis (FSP) of iron acelylacetonale in xylene/acetonitrile solutions, and the resulting aerosol was in situ coaled with SiO2 by oxidation of swirling hexamethlydisiloxane vapor. The process allows independent control of the core Fe2O3, particle properties and the thickness of their silica coaling film. This ensures that the non-magnetic SiO2 layer can be closely controlled and minimized. The optimal SiO2 content for complete (hermetic) encapsulation of the magnetic core particles was determined by isopropanol chemisorption. The magnetization of Fe2O3 coated with about 2 nm thin SiO2 layers was nearly identical lo that of uncoated, pure Fe2O3 nanoparlicles.

Hermetically coated superparamagnetic Fe2O3 particles with SiO2 nanofilms

Magnetic nanoparticles are frequently coated with SiO2 to improve their functionality and biocom-patibility in a range of biomedical and polymer nanocomposite applications. In this paper, a scalable flame aerosol technology is used to produce highly dispersible, superparamagnetic iron oxide nanoparticles hermetically coated with silica to retain full magnetization performance. Iron oxide particles were produced by flame spray pyrolysis of iron acetylacetonate in xylene/acetonitrile solutions and the resulting aerosol was in situ coated with silicon dioxide by oxidation of swirling hexamethlydisiloxane vapor. The process allows independent control of the core Fe2O3 (maghemite) particle properties and the thickness of their silica coating film. This ensures that the nonmagnetic SiO2 layer can be closely controlled and minimized. The optimal SiO2 content for complete (hermetic) encapsulation of the magnetic core particles was determined by isopropanol chemisorption. The magnetization of Fe 2O3 coated with about 2 nm thin SiO2 layers was nearly identical to that of uncoated, pure Fe2O3 nanoparticles. © 2009 American Chemical Society.

Fabrication and properties of TBCCO films via air-atomising spray deposition of thallium-free precursors

The high-field properties of polycrystalline superconducting TlBaCaCuO films fabricated by the incorporation of thallium vapour into air-atomised BaCaCuO precursors are described. Thick films with Tc values in the range 106-111 K have been prepared on polycrystalline yttria-stabilised zirconia substrates. The surface morphology, crystal structure and composition of the films are related to their high-field transport and magnetisation properties. Typical 10 mm × 9 mm films show Jc values > 1×104 A/cm2 at 77 K (0 T). The best film has a Jc=1.3×104 A/cm2 (Ic=3.6 A) at 77 K (0 T). Films prepared on 26 mm×9 mm substrates show typical large-area Jc values > 0.5×104 A/cm2 (77 K, 0 T). A square planar specimen of dimensions 4.3 mm ×4.3 mm exhibited magnetisation Jc values=1.2×105 A/cm2 at 4.2 K (0.1 T), 9.3×104 A/cm2 at 10 K (0.1 T), 3.3×104 A/ cm2 at 4 K (8 T), and 1.6×104 A/cm2 at 10 K (8 T). © 1994.