Cadmium leachability and microbial population dynamics in a stabilized and bioaugmented model contaminated soil

This article presents a laboratory study on the consequences of the application of combined soil stabilization and bioaugmentation in the remediation of a model contaminated soil. Stabilization and bioaugmentation are two techniques commonly applied independently for the remediation of heavy metal and organic contamination respectively. However, for a cocktail of contaminants combined treatments are currently being considered. The model soil was contaminated with a cocktail of organics and heavy metals based on the soil and contaminant conditions in a real contaminated site. The soil stabilization treatment was applied using either zeolite or green waste compost as additives and a commercially available hydrocarbon degrading microbial consortium was used for the bioaugmentation treatment. The effects of stabilization with or without bioaugmentation on the leachability of cadmium and copper was observed using an EU batch leaching test procedure and a flow-through column leaching test, both using deionized water at a pH of 5.6. In addition, the population of hydrocarbon degrading microorganisms was monitored using a modified plate count procedure in cases where bioaugmentation was applied. It was found that while the stabilization treatment reduced the metal leachability by up to 60%, the bioaugmentation treatment increased it by up to 100% Microbial survival was also higher in the stabilized soil samples.

Innovative fabrication of PZT pillar arrays by a colloidal approach

An innovative approach for fabricating pillar arrays for ultrasonic transducer applications is disclosed. It involves the preparation of concentrated piezoelectric lead zirconate titanate (PZT) suspensions in aqueous solutions of epoxy resin and its polymerization upon adding a polyamine based hardener. Zeta potential and rheological measurements revealed that 1wt.% dispersant, 20wt.% of epoxy resin and a hardener/epoxy resin ratio of 0.275mLg -1, were the optimized contents to obtain strong PZT samples with high green strength (35.21±0.39MPa). Excellent ellipsoidal and semi-circle shaped pillar arrays presenting lateral dimensions lower than 10μm and 100μm height were successfully achieved. The organics burning off was conducted at 500°C for 2h at a heating rate of 1°Cmin -1. Sintering was then carried out in the same heating cycle at 1200°C for 1h. The microstructures of the green and sintered ceramics were homogeneous and no large defects could be detected. © 2011 Elsevier Ltd.