The temperature dependence of effective thermal conductivity of open-celled steel alloy foams

The effective thermal conductivity of steel alloy FeCrAlY (Fe-20 wt.% Cr-5 wt.% Al-2 wt.% Y-20 wt.%) foams with a range of pore sizes and porosities was measured between 300 and 800 K, under both vacuum and atmospheric conditions. The results show that the effective thermal conductivity increases rapidly as temperature is increased, particularly in the higher temperature range (500-800 K) where the transport of heat is dominated by thermal radiation. The effective conductivity at temperature 800 K can be three times higher than that at room temperature (300 K). Results obtained under vacuum conditions reveal that the effective conductivity increases with increasing pore size or decreasing porosity. The contribution of natural convection to heat conduction was found to be significant, with the effective thermal conductivity at ambient pressure twice the value of vacuum condition. The results also show that natural convection in metal foams is strongly dependent upon porosity. © 2003 Elsevier B.V. All rights reserved.

In situ characterization of alloy catalysts for low-temperature graphene growth.

Low-temperature (∼450 °C), scalable chemical vapor deposition of predominantly monolayer (74%) graphene films with an average D/G peak ratio of 0.24 and domain sizes in excess of 220 μm(2) is demonstrated via the design of alloy catalysts. The admixture of Au to polycrystalline Ni allows a controlled decrease in graphene nucleation density, highlighting the role of step edges. In situ, time-, and depth-resolved X-ray photoelectron spectroscopy and X-ray diffraction reveal the role of subsurface C species and allow a coherent model for graphene formation to be devised.

Progress in the understanding of Ni silicide formation for advanced MOS structures

Metallic silicides have been used as contact materials on source/drain and gate in metal-oxide semiconductor (MOS) structure for 40 years. Since the 65 nm technology node, NiSi is the preferred material for contact in microelectronic due to low resistivity, low thermal budget, and low Si consumption. Ni(Pt)Si with 10 at.% Pt is currently employed in recent technologies since Pt allows to stabilize NiSi at high temperature. The presence of Pt and the very low thickness (<10 nm) needed for the device contacts bring new concerns for actual devices. In this work, in situ techniques [X-ray diffraction (XRD), X-ray reflectivity (XRR), sheet resistance, differential scanning calorimetry (DSC)] were combined with atom probe tomography (APT) to study the formation mechanisms as well as the redistribution of dopants and alloy elements (Pt, Pd.) during the silicide formation. Phenomena like nucleation, lateral growth, interfacial reaction, diffusion, precipitation, and transient phase formation are investigated. The effect of alloy elements (Pt, Pd.) and dopants (As, B.) as well as stress and defects induced by the confinement in devices on the silicide formation mechanism and alloying element redistribution is examined. In particular APT has been performed for the three-dimensional (3D) analysis of MOSFET at the atomic scale. The advances in the understanding of the mechanisms of formation and redistribution are discussed. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Ni(Pt)-silicide contacts on CMOS devices: Impact of substrate nature and Pt concentration on the phase formation

Ni silicides used as contacts in source/drain and gate of advanced CMOS devices were analyzed by atom probe tomography (APT) at atomic scale. These measurements were performed on 45 nm nMOS after standard self-aligned silicide (salicide) process using Ni(5 at.% Pt) alloy. After the first annealing (RTA1), δ-Ni2Si was the only phase formed on gate and source/drain while, after the second annealing (RTA2), two different Ni silicides have been formed: NiSi on the gate and δ-Ni2Si on the source and drain. This difference between source/drain and gate regions in nMOS devices has been related to the Si substrate nature (poly or mono-crystalline) and to the size of the contact. In fact, NiSi seems to have difficulties to nucleate in the narrow source/drain contact on mono-crystalline Si. The results have been compared to analysis performed on 28 nm nMOS where the Pt concentration is higher (10 at.% Pt). In this case, θ-Ni2Si is the first phase to form after RTA1 and NiSi is then formed at the same time on source (or drain) and gate after RTA2. The absence of the formation of NiSi from δ-Ni 2Si/Si(1 0 0) interface compared to θ-Ni2Si/Si(1 0 0) interface could be related to the difference of the interface energies. The redistributions of As and Pt in different silicides and interfaces were measured and discussed. In particular, it has been evidenced that Pt redistributions obtained on both 45 and 28 nm MOS transistors correspond to respective Pt distributions measured on blanket wafers. © 2013 Elsevier B.V. All rights reserved.