Efficient carbon nanotube field emitter using electrospun carbon nanofibers as a flexible electrode

Thermal-stable, conductive, and flexible carbon fabric (CF), which is composed of thin carbon fibers prepared by electrospinning, was used for the substrate of carbon nanotube (CNT) field emitter arrays. The field emitter arrays were prepared by chemical vapor deposition (CVD). The current density-electric field characteristics revealed that the CNT field emitter arrays on CF produced a higher current density at a lower turn-on voltage compared to ones on a Si substrate. This emitter integrated with a gate electrode based on hierarchy-structured carbon materials, CNTs on CF, can be used for light sources, displays, and other electronic devices. © 2009 Materials Research Society.

Wet-spinning of amyloid protein nanofibers into multifunctional high-performance biofibers.

Amyloid nanofibers derived from hen egg white lysozyme were processed into macroscopic fibers in a wet-spinning process based on interfacial polyion complexation using a polyanionic polysaccharide as cross-linker. As a result of their amyloid nanostructure, the hierarchically self-assembled protein fibers have a stiffness of up to 14 GPa and a tensile strength of up to 326 MPa. Fine-tuning of the polyelectrolytic interactions via pH allows to trigger the release of small molecules, as demonstrated with riboflavin-5'-phophate. The amyloid fibrils, highly oriented within the gellan gum matrix, were mineralized with calcium phosphate, mimicking the fibrolamellar structure of bone. The formed mineral crystals are highly oriented along the nanofibers, thus resulting in a 9-fold increase in fiber stiffness.

Ultrasmall microlens array based on vertically aligned carbon nanofibers.

An ultrasmall tunable microlens with a diameter of 1.5 μm is fabricated using nematic liquid crystals (electrically tunable medium) and vertically aligned carbon nanofibers (CNFs, electrodes). Individual CNFs are grown at the center of circular dielectric regions. This allows the CNFs to produce a more Gaussian electric field profile and hence more uniformity in lens array switching.

Effects of pre-treatment and plasma enhancement on chemical vapor deposition of carbon nanotubes from ultra-thin catalyst films

We report a detailed study of surface-bound chemical vapor deposition of carbon nanotubes and nanofibers from evaporated transition metal catalysts exposed to ammonia diluted acetylene. We show that a reduction of the Fe/Co catalyst film thickness below 3 nm results into a transition from large diameter (> 40 nm), bamboo-like nanofibers to small diameter (similar to 5 nm) multi-walled carbon nanotubes. The nanostructuring of ultrathin catalyst films critically depends on the gas atmosphere, with the resulting island distribution initiating the carbon nucleation. Compared to purely thermal chemical vapor deposition, we find that, for small diameter nanotube growth, DC plasma assistance is detrimental to graphitization and sample homogeneity and cannot prevent an early catalyst poisoning. (c) 2006 Elsevier B.V. All rights reserved.

High current density nanofilament cathodes for microwave amplifiers

The fabrication of high current density nanofilament cathodes for microwave amplifiers was discussed. Metallic nanowires grown on silicon wafers and carbon nanotubes/nanofibers grown by catalytic plasma enhanced chemical vapor deposition (PECVD) were the two types of nanofilament arrays analyzed as cathodes materials. It was observed that the arrays of 5.8 μm height and 50 nm diameter carbon nanotubes exhibited geometrical enhancement factor of 240+-7.5%. The results show that carbon nanotubes/nanofibers arrays are best suited for nanofilament cathodes.