Modelling failure of composite specimens with defects under compression loading

Composite structures exhibit many different failure mechanisms, but attempts to model composite failure frequently make a priori assumptions about the mechanism by which failure will occur. Wang et al. [1] conducted compressive tests on four configurations of composite specimen manufactured with out-of-plane waviness created by ply-drop defects. There were significantly different failures for each case. Detailed finite element models of these experiments were developed which include competing failure mechanisms. The model predictions correlate well with experimental results-both qualitatively (location of failure and shape of failed specimen) and quantitatively (failure load). The models are used to identify the progression of failure during the compressive tests, determine the critical failure mechanism for each configuration, and investigate the effect of cohesive parameters upon specimen strength. This modelling approach which includes multiple competing failure mechanisms can be applied to predict failure in situations where the failure mechanism is not known in advance. © 2013 Elsevier Ltd. All rights reserved.

Tensile strength of UD-composite laminates with multiple holes

The residual strength of glass fibre reinforced vinyl-ester laminates with multiple holes was investigated through an experimental programme. Different types of structured hole patterns and hole densities were investigated and analysed using digital image correlation strain measuring technique. Three different failure modes could be observed when the hole patterns and the hole densities were a altered. These three failure modes were used as the foundation for a simple yet effective analytical model in order to predict the residual strength of damaged composite specimens. Finally, a number of laminates with randomly distributed holes were tested experimentally. The analytical model can predict the failure mode and failure strength of the experiments with sufficiently good fidelity. © 2010 Elsevier Ltd.

Strength of GRP-laminates with multiple fragment damages

The strength of glass fibre reinforced vinyl-ester laminates with multiple holes has been investigated experimentally. Different hole pattern configurations have been tested, primarily for unidirectional laminates. Unidirectional laminates have shown very low notch sensitivity and the laminate failure was governed by two competing failure modes; shear off failure and net section tensile failure.