Direct observation of the structural component of the metal-insulator phase transition and growth habits of epitaxially grown VO2 nanowires.

We have grown epitaxially orientation-controlled monoclinic VO2 nanowires without employing catalysts by a vapor-phase transport process. Electron microscopy results reveal that single crystalline VO2 nanowires having a [100] growth direction grow laterally on the basal c plane and out of the basal r and a planes of sapphire, exhibiting triangular and rectangular cross sections, respectively. In addition, we have directly observed the structural phase transition of single crystalline VO2 nanowires between the monoclinic and tetragonal phases which exhibit insulating and metallic properties, respectively, and clearly analyzed their corresponding relationships using in situ transmission electron microscopy.

Surface-stress-induced Mott transition and nature of associated spatial phase transition in single crystalline VO2 nanowires.

We demonstrate that the Mott metal-insulator transition (MIT) in single crystalline VO(2) nanowires is strongly mediated by surface stress as a consequence of the high surface area to volume ratio of individual nanowires. Further, we show that the stress-induced antiferromagnetic Mott insulating phase is critical in controlling the spatial extent and distribution of the insulating monoclinic and metallic rutile phases as well as the electrical characteristics of the Mott transition. This affords an understanding of the relationship between the structural phase transition and the Mott MIT.

The use of C-V techniques to investigate instability mechanisms in M-I-S structures

In the field of flat panel displays, the current leading technology is the Active Matrix liquid Crystal Display; this uses a-Si:H based thin film transistors (TFTs) as the switching element in each pixel. However, under gate bias a-Si:H TFTs suffer from instability, as is evidenced by a shift in the gate threshold voltage. The shift in the gate threshold voltage is generally measured from the gate transfer characteristics, after subjecting the TFT to prolonged gate bias. However, a major drawback of this measurement method is that it cannot distinguish whether the shift is caused by the change in the midgap states in the a-Si:H channel or by charge trapping in the gate insulator. In view of this, we have developed a capacitance-voltage (C-V) method to measure the shift in threshold voltage. We employ Metal-Insulator-Semiconductor (MIS) structures to investigate the threshold voltage shift as they are simpler to fabricate than TFTs. We have investigated a large of number Metal/a-Si:H/Si3N4/Si+n structures using our C-V technique. From, the C-V data for the MIS structures, we have found that the relationship between the thermal energy and threshold voltage shift is similar to that reported by Wehrspohn et. al in a-Si:H TFTs (J Appl. Phys, 144, 87, 2000). The a-Si:H and Si3N4 layers were grown using the radio-frequency plasma-enhanced chemical vapour deposition technique.

Picosecond laser patterning of PEDOT:PSS thin films

Picosecond pulsed laser (10.4 ps, 1064 nm, 5 and 50 kHz) patterning studies were performed, of PEDOT:PSS thin films of varying thickness deposited by spin coating on glass substrates, by ablating the films or by changing locally by laser irradiation the optical and electrical properties of the polymer. From a detailed observation of the morphology of single pulse ablated holes on the surfaces of the films, in combination with simple calculations, it is concluded that photomechanical ablation is the likely ablation mechanism of the films. The single pulse ablation thresholds were measured equal to 0.13-0.18 J/cm 2 for films with thicknesses in the region of ∼100-600 nm. The implications on ablation line patterning of the films using different fluences, scanning speeds and pulse repetition rates, were investigated systematically. Laser irradiation of the films before ablation induces a metal-insulator transition of the polymer because of the formation of charge localization due to a possible creation of molecular disorder in the polymer and shortening of its conjugation length. © 2010 Elsevier B.V. All rights reserved.