Growth of highly-quality single-wall carbon nanotubes without amorphous carbon formation

A simple way to deposit single-wall carbon nanotubes by CVD without the co-deposition of unwanted a-C was demonstrated. It was found that the catalytic deposition of SWCNTs occurs at a substantial rate compared to the self-pyrolysis of the hydrocarbon gas used.

Advantages of top-gate, high-k dielectric carbon nanotube field-effect transistors

The subthreshold slope, transconductance, threshold voltage, and hysteresis of a carbon nanotube field-effect transistor (CNT FET) were examined as its configuration was changed from bottom-gate exposed channel, bottom-gate covered channel to top-gate FET. An individual single wall CNT was grown by chemical vapor deposition and its gate configuration was changed while determining its transistor characteristics to ensure that the measurements were not a function of different chirality or diameter CNTs. The bottom-gate exposed CNT FET utilized 900 nm SiO2 as the gate insulator. This CNT FET was then covered with TiO2 to form the bottom-gate covered channel CNT FET. Finally, the top-gate CNT FET was fabricated and the device utilized TiO 2 (K ∼ 80, equivalent oxide thickness=0.25 nm) as the gate insulator. Of the three configurations investigated, the top-gate device exhibited best subthreshold slope (67-70 mV/dec), highest transconductance (1.3 μS), and negligible hysteresis in terms of threshold voltage shift. © 2006 American Institute of Physics.

Carbon nanotube Schottky diode and directionally dependent field-effect transistor using asymmetrical contacts

We demonstrate the fabrication and operation of a carbon nanotube (CNT) based Schottky diode by using a Pd contact (high-work-function metal) and an Al contact (low-work-function metal) at the two ends of a single-wall CNT. We show that it is possible to tune the rectification current-voltage (I-V) characteristics of the CNT through the use of a back gate. In contrast to standard back gate field-effect transistors (FET) using same-metal source drain contacts, the asymmetrically contacted CNT operates as a directionally dependent CNT FET when gated. While measuring at source-drain reverse bias, the device displays semiconducting characteristics whereas at forward bias, the device is nonsemiconducting. © 2005 American Institute of Physics.

Self-aligned, gated arrays of individual nanotube and nanowire emitters

We demonstrate the production of integrated-gate nanocathodes which have a single carbon nanotube or silicon nanowire/whisker per gate aperture. The fabrication is based on a technologically scalable, self-alignment process in which a single lithographic step is used to define the gate, insulator, and emitter. The nanotube-based gated nanocathode array has a low turn-on voltage of 25 V and a peak current of 5 μA at 46 V, with a gate current of 10 nA (i.e., 99% transparency). These low operating voltage cathodes are potentially useful as electron sources for field emission displays or miniaturizing electron-based instrumentation.