Ni-silicide growth kinetics in Si and Si/SiO2 core/shell nanowires.

A systematic study of the kinetics of axial Ni silicidation of as-grown and oxidized Si nanowires (SiNWs) with different crystallographic orientations and core diameters ranging from ∼ 10 to 100 nm is presented. For temperatures between 300 and 440 °C the length of the total axial silicide intrusion varies with the square root of time, which provides clear evidence that the rate limiting step is diffusion of Ni through the growing silicide phase(s). A retardation of Ni-silicide formation for oxidized SiNWs is found, indicative of a stress induced lowering of the diffusion coefficients. Extrapolated growth constants indicate that the Ni flux through the silicided NW is dominated by surface diffusion, which is consistent with an inverse square root dependence of the silicide length on the NW diameter as observed for (111) orientated SiNWs. In situ TEM silicidation experiments show that NiSi(2) is the first forming phase for as-grown and oxidized SiNWs. The silicide-SiNW interface is thereby atomically abrupt and typically planar. Ni-rich silicide phases subsequently nucleate close to the Ni reservoir, which for as-grown SiNWs can lead to a complete channel break-off for prolonged silicidation due to significant volume expansion and morphological changes.

Elastic properties of crystalline-amorphous core-shell silicon nanowires

The pressure behavior of Raman frequencies and line widths of crystalline core-amorphous shell silicon nanowires (SiNWs) with two different core-to-shell ratio thicknesses was studied at pressures up to 8 GPa. The obtained isothermal compressibility (bulk modulus) of SiNWs with a core-to-shell ratio of about 1.8 is ∼20% higher (lower) than reported values for bulk Si. For SiNWs with smaller core-to-shell ratios, a plastic deformation of the shell was observed together with a strain relaxation. A significant increase in the full width at half-maximum of the Raman LTO-peak due to phonon decay was used to determine the critical pressure at which LTO-phonons decay into LO + TA phonons. Our results reveal that this critical pressure in strained core-shell SiNWs (∼4 GPa) is different from the reported value for bulk Si (∼7 GPa), whereas no change is observed for relaxed core-shell SiNWs. © 2013 American Chemical Society.

Resonant excitation and imaging of nonequilibrium exciton spins in single core-shell GaAs-AlGaAs nanowires.

Nonequilibrium spin distributions in single GaAs/AlGaAs core-shell nanowires are excited using resonant polarized excitation at 10 K. At all excitation energies, we observe strong photoluminescence polarization due to suppressed radiative recombination of excitons with dipoles aligned perpendicular to the nanowire. Excitation resonances are observed at 1- or 2-LO phonon energies above the exciton ground states. Using rate equation modeling, we show that, at the lowest energies, strongly nonequilibrium spin distributions are present and we estimate their spin relaxation rate.

Temperature dependence of photoluminescence from single core-shell GaAs-AlGaAs nanowires

Temperature-dependent polarized microphotoluminescence measurements of single GaAsAlGaAs core-shell nanowires are used to probe their electronic states. The low-temperature emission from these wires is strongly enhanced compared with that observed in bare GaAs nanowires and is strongly polarized, reflecting the dielectric mismatch between the nanowire and the surrounding air. The temperature-dependent band gap of the nanowires is seen to be somewhat different from that observed in bulk GaAs, and the PL rapidly quenches above 120 K, with an activation energy of 17 meV reflecting the presence of nonradiative defects. © 2006 American Institute of Physics.

High-resolution TEM characterization of ZnO core-shell nanowires for dye-sensitized solar cells

Recently ZnO nanowire films have been used in very promising and inexpensive dye-sensitized solar cells (DSSC). It was found that the performance of the devices can be enhanced by functionalising the nanowires with a thin metal oxide coating. This nm-scale shell is believed to tailor the electronic structure of the nanowire, and help the absorption of the dye. Core-shell ZnO nanowire structures are synthesised at low temperature (below 120°C) by consecutive hydrothermal growth steps. Different materials are investigated for the coating, including Mg, Al, Cs and Zr oxides. High resolution TEM is used to characterise the quality of both the nanowire core and the shell, and to monitor the thickness and the degree of crystallisation of the oxide coating. The interface between the nanowire core and the outer shell is investigated in order to understand the adhesion of the coating, and give valuable feedback for the synthesis process. Nanowire films are packaged into dye-sensitised solar cell prototypes; samples coated with ZrO2 and MgO show the largest enhancement in the photocurrent and open-circuit voltage and look very promising for further improvement. © 2010 IOP Publishing Ltd.

Advantages of top-gate, high-k dielectric carbon nanotube field-effect transistors

The subthreshold slope, transconductance, threshold voltage, and hysteresis of a carbon nanotube field-effect transistor (CNT FET) were examined as its configuration was changed from bottom-gate exposed channel, bottom-gate covered channel to top-gate FET. An individual single wall CNT was grown by chemical vapor deposition and its gate configuration was changed while determining its transistor characteristics to ensure that the measurements were not a function of different chirality or diameter CNTs. The bottom-gate exposed CNT FET utilized 900 nm SiO2 as the gate insulator. This CNT FET was then covered with TiO2 to form the bottom-gate covered channel CNT FET. Finally, the top-gate CNT FET was fabricated and the device utilized TiO 2 (K ∼ 80, equivalent oxide thickness=0.25 nm) as the gate insulator. Of the three configurations investigated, the top-gate device exhibited best subthreshold slope (67-70 mV/dec), highest transconductance (1.3 μS), and negligible hysteresis in terms of threshold voltage shift. © 2006 American Institute of Physics.