The microstructure and mechanical properties of ball-milled stainless steel powder: The effect of hot-pressing vs. laser sintering

The microstructure and mechanical properties of sintered stainless steel powder, of composition AISI 420, have been measured. Ball-milled powder comprising nanoscale grains was sintered to bulk specimens by two alternative routes: hot-pressing and microlaser sintering. The laser-sintered alloy has a porosity of 6% and comprises a mixture of delta ferrite and tempered martensite, and the relative volume fraction varies along the axis of the specimen due to a thermal cycle that evolves with progressive deposition. In contrast, the hot-pressed alloy has a porosity of 0.7% and exhibits a martensitic lath structure with carbide particles at the boundaries of the prior austenite grains. These differences in microstructure lead to significant differences in mechanical properties. For example, the uniaxial tensile strength of the hot-pressed material is one-half of its compressive strength, due to void initiation at the carbide particles at the prior austenite grain boundaries. Nanoindentation measurements reveal a size effect in hardness and also reveal the sensitivity of hardness to the presence of mechanical polishing and electropolishing. © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

The role of damping in steel pan manufacture

Results are presented of systematic studies of vibration damping in steel of a type, and processed by a route, rel-evant to Caribbean steel pans. Damping is likely to be a significant factor in the variation of sound quality be-tween different pans. The main stages in pan manufac-ture are simulated in a controlled manner using sheet steel, cold-rolled to a prescribed level of thickness reduc-tion then annealed at a chosen temperature in a laboratory furnace. Small test strips were cut from the resulting material, and tested in free-free beam bending to deduce the Young’s modulus and its associated loss factor. It is shown that the steel type, the degree of cold working and the annealing temperature all have a significant influence on damping. Furthermore, for each individual specimen damping is found to decrease with rising frequency, ap-proximately following a power law. Comparison with samples cut from a real pan show that there are further influences from the pan’s geometrical details.

Stainless steel sandwich

The Cambridge University's Gordon Laboratory, in collaboration with Fibertech and the Defence Science and Technology Laboratory in the UK, has developed a novel melt spun fiber bore called 'Fibrecore', fabricated entirely from stainless steel with thin faceplates. Fibrecore is typically manufactured by 5mm-long and 70μm thick stainless steel fibers, produced by a melt overflow process. Its entirely metallic construction allows spot welding and tungsten inert gas welding without difficulty. Fibrecore exhibits different energy absorption mechanisms such as core cushioning, core-faceplate delamination, and plastic faceplate deformation, often in a concertina-like fashion. Its low-cost, high structural efficiency and good energy absorption characteristics make it attractive for a range of commercial and military applications. Such applications being evaluated include vehicle body panels, exhaust system noise reduction, low cost filters, and lightweight physical protection. In addition to these characteristics, Fibrecore exhibits properties such as corrosion protection, vibrational damping, and thermal insulation, which also extend its applications.