Erosion-corrosion of mild steel in a temperature gradient

Thinning of heat-exchanger tubes by erosion-corrosion has been a problem in fluidized bed combustors (FBCs), particularly at lower metal temperatures where thicker, mechanically protective oxide scales are unable to form. Many laboratory-scale tests have shown a decrease in material loss at higher temperatures, in a similar manner to FBC boilers, but also show a decrease in wastage at low temperatures (e.g. 200°C) which has not been detected in boilers. It has been suggested that this difference is due to laboratory tests being carried out isothermally whereas in a FBC boiler the fluidized bed is considerably hotter than the metal heat exchanger tubing. In this laboratory study the simulation was therefore improved by internally cooling one of the two low carbon steel specimens. These were rotated in a horizontal plane within a lightly fluidized bed with relative particle velocities of 1.3-2.5 m s-1. Tests were carried out over a range of bed temperatures (200-500°C) and cooled specimen surface temperatures (115-500°C), with a maximum temperature difference between the two of 320°C. Although specimens exposed isothermally still showed maximum wastage at intermediate temperatures (about 350°C), those which were cooled showed high levels of wastage at temperatures as low as 200°C in a similar manner to FBC boilers. Cooling may modify the isothermal erosion-corrosion curve, causing it to broaden and the maximum wastage rate to shift to lower temperatures. © 1995.

Wastage of low alloy steels in a fluidized bed environment

The wastage behaviour of four low alloy steels, suitable for use as evaporator tubing in industrial atmospheric fluidized bed combustors (AFBCs), was examined in a laboratory-scale test rig. Specimens exposed in the test apparatus experienced a high flux of impacts at low particle velocities similar to conditions in a FBC boiler. The influence of time, velocity and temperature on the wastage behaviour was examined and incubation times and velocity exponents were determined and their values discussed. Since high-temperature oxidation played an important role in this process, the short-term oxidation rate of each of the steels was measured. The mechanisms of material loss across the temperature range were discussed and the behaviour of the low alloy steels in the current work was compared with that of high alloy and stainless steels in earlier studies. © 1995.

Laboratory-scale fluidized bed rig for high-temperature tube wastage studies

As part of a study of the wear of candidate heat exchanger tube materials for use in fluidized bed combustors, two similar laboratory-scale rigs have been built and characterized. Specimens of selected alloys are carried on counter-rotating rotors immersed in a fluidized bed, and are exposed to particle impact velocities of up to approximately 3 ms-1 at temperatures up to 1000°C. The performance of this design of apparatus has been investigated in detail. The effects of several experimental variables have been studied, including angle of particle impact, specimen speed, position of the rotor within the fluidized bed, duration of exposure, bed material particle size, degradation of the bed material, degree of fluidization of the bed, and size of specimen. In many cases the results obtained with steel specimens at elevated temperatures are similar to those observed with polymeric specimens at low temperatures.