Impact of hydrated magnesium carbonate additives on the carbonation of reactive MgO cements

Reactive magnesia (MgO) cements have emerged as a potentially more sustainable and technically superior alternative to Portland cement due to their lower production temperature and ability to sequester significant quantities of CO2. Porous blocks containing MgO were found to achieve higher strength values than PC blocks. A number of variables are investigated to achieve maximum carbonation and associated high strengths. This paper focuses on the impact of four different hydrated magnesium carbonates (HMCs) as cement replacements of either 20 or 50%. Accelerated carbonation (20 C, 70-90% RH, 20% CO2) is compared with natural curing (20 C, 60-70% RH, ambient CO2). SEM, TG/DTA, XRD, and HCl acid digestion are utilized to provide a thorough understanding of the performance of MgO-cement porous blocks. The presence of HMCs resulted in the formation of larger size carbonation products with a different morphology than those in the control mix, leading to significantly enhanced carbonation and strength. © 2013 Elsevier Ltd.

Characterization of light and heavy hydrated magnesium carbonates using thermal analysis

Upon heating, hydrated magnesium carbonates (HMCs) undergo a continuous sequence of decomposition reactions. This study aims to investigate the thermal decomposition of various commercially produced HMCs classified as light and heavy, highlight their differences, and provide an insight into their compositions in accordance with the results obtained from thermal analysis and microstructure studies. An understanding of the chemical compositions and microstructures, and a better knowledge of the reactions that take place during the decomposition of HMCs were achieved through the use of SEM, XRD, and TG/differential thermal analysis (DTA). The quantification of their CO 2 contents was provided by TG and dissolving the samples in HCl acid. Results show that variations exist within the microstructure and decomposition patterns of the two groups of HMCs, which do not exactly fit into the fixed stoichiometry of the known HMCs in the MgO-CO2-H2O system. The occurrence of an exothermic DTA peak was only observed for the heavy HMCs, which was attributed to their high CO2 contents and the relatively delayed decomposition pattern. © 2013 Akadémiai Kiadó, Budapest, Hungary.

Enhancing the carbonation of MgO cement porous blocks through improved curing conditions

The use of reactive magnesia (MgO) as the binder in porous blocks demonstrated significant advantages due to its low production temperatures and ability to carbonate, leading to significant strengths. This paper investigates the enhancement of the carbonation process through different curing conditions: water to cement ratio (0.6-0.9), CO2 concentration (5-20%), curing duration (1-7 days), relative humidity (55-98%), and wet/dry cycling frequency (every 0-3 days), improving the carbonation potential through increased amounts of CO2 absorbed and enhanced mechanical performance. UCS results were supported with SEM, XRD, and HCl acid digestion analyses. The results show that CO2 concentrations as low as 5% can produce the required strengths after only 1 day. Drier mixes perform better in shorter curing durations, whereas larger w/c ratios are needed for continuous carbonation. Mixes subjected to 78% RH outperformed all the others, also highlighting the benefits of incorporating wet/dry cycling to induce carbonation. © 2014 Elsevier Ltd.