Polarisation dependent all-optical nonlinearity far from the bandedge in active GaAs/AlGaAs quantum well waveguides

This paper describes a measurement on a GaAs quantum well waveguide with a high built in field across the quantum wells at a wavelength far from the bandedge. The device structure used for the measurement has been fabricated at STC Technology Ltd and is that of a standard laser ridge structure. In fabrication double heterostructure layers are grown on a [001] n + GaAs substrate, with the active region containing two intrinsic GaAs quantum wells of 10nm thickness separated by 10nm. A 4μm wide ridge is etched to provide transverse optical guiding. The experimental work has involved the use of 1.06μm wavelength light from a Q-switched Nd:YAG laser. Any induced change in refractive index is determined by measuring the change in transmission of the quantum well waveguide Fabry-Perot cavity. The waveguide is placed on a Peltier temperature controller to allow thermal tuning.

Vertically standing Ge nanowires on GaAs(110) substrates.

The growth of epitaxial Ge nanowires is investigated on (100), (111) B and (110) GaAs substrates in the growth temperature range from 300 to 380 °C. Unlike epitaxial Ge nanowires on Ge or Si substrates, Ge nanowires on GaAs substrates grow predominantly along the [Formula: see text] direction. Using this unique property, vertical [Formula: see text] Ge nanowires epitaxially grown on GaAs(110) surface are realized. In addition, these Ge nanowires exhibit minimal tapering and uniform diameters, regardless of growth temperatures, which is an advantageous property for device applications. Ge nanowires growing along the [Formula: see text] directions are particularly attractive candidates for forming nanobridge devices on conventional (100) surfaces.

Laser microstructuring of Si surfaces for low-threshold field-electron emission

Dense arrays of high aspect ratio Si micro-pyramids have been formed by cumulative high intensity laser irradiation of doped Si wafers in an SF6 environment. A comparative study using nanosecond (XeCl, 308 nm) and femtosecond (Ti: Sapphire, 800 nm and KrF, 248 nm) laser pulses has been performed in this work. The influence of pulse duration and ambient gas pressure (SF6) is also presented. Scanning electron microscopy has shown that upon laser irradiation conical features appear on the Si surface in a rather homogenous distribution and with a spontaneous self alignment into arrays. Their lowest tip diameter is 800 nm; while their height reaches up to 90 mum. Secondary tip decoration appears on the surface of the formed spikes. Areas of 2 X 2 mm(2) covered with Si cones have been tested as cold cathode field emitters. After several conditioning cycles, the field emission threshold for the studied Si tips is as low as 2 V/mum, with an emission current of 10(-3) A/cm(2) at 4 V/mum. Even though these structures have smaller aspect ratios than good quality carbon nanotubes, their field emission properties are similar. The simple and direct formation of field emission Si arrays over small pre-selected areas by laser irradiation could lead to a novel approach for the development of electron sources. (C) 2003 Elsevier B.V. All rights reserved.