Hydrogenated amorphous silicon and silicon nitride deposited at less than 100° C by ECR-PECVD for thin film transistors

A systematic study has been made of the growth of both hydrogenated amorphous silicon (a-Si:H) and silicon nitride (a-SiN) by electron cyclotron resonance plasma enhanced chemical vapour deposition (ECR-PECVD). In the case of a-SiN, helium and nitrogen gas is injected into the system such that it passes through the resonance zone. These highly ionised gases provide sufficient energy to ionise the silane gas, which is injected further downstream. It is demonstrated that a gas phase reaction occurs between the silane and nitrogen species. It is control of the ratio of silane to nitrogen in the plasma which is critical for the production of stoichiometric a-SiN. Material has been produced at 80°C with a Si:N ratio of 1:1.3 a breakdown strength of ∼6 MV cm-1 and resistivity of > 1014 Ω cm. In the case of a-Si:H, helium and hydrogen gas is injected into the ECR zone and silane is injected downstream. It is shown that control of the gas phase reactions is critical in this process also. a-Si:H has been deposited at 80 °C with a dark conductivity of 10-11 Ω-1 cm-1 and a photosensitivity of justbelowl 4×104. Such materials are suitable for use in thin film transistors on plastic substrates.

Synthesis of 10 nm Ag nanoparticle polymer composite pastes for low temperature production of high conductivity films

The conversion of silver nanoparticle (NP) paste films into highly conductive films at low sintering temperature is an important requirement for the developing areas of additive fabrication and printed electronics. Ag NPs with a diameter of ∼10 nm were prepared via an improved chemical process to produce viscous paste with a high wt%. The paste consisted of as-prepared Ag NP and an organic vehicle of ethylcellulose that was deposited on glass and Si substrates using a contact lithographic technique. The morphology and conductivity of the imprinted paste film were measured as a function of sintering temperature, sintering time and the percentage ratio of Ag NP and ethylcellulose. The morphology and conductivity were examined using scanning electron microscopy (SEM) and a two-point probe electrical conductivity measurement. The results show that the imprinted films were efficiently converted into conducting states when exposed to sintering temperature in the range of 200-240 °C, this temperature is lower than the previously reported values for Ag paste. © 2010 Elsevier B.V. All rights reserved.