Material properties and tribological performance of rf-PECVD deposited DLC coatings

Diamond-like carbon (DLC) coatings were deposited on to silicon, glass and metal substrates, using an rf-plasma enhanced chemical vapour deposition (rf-PECVD) process. The resultant film properties were evaluated in respect of material and interfacial property control, based on bias voltage variation and the introduction of inert (He and Ar) and reactive (N2) diluting gases in a CH4 plasma. The analysis techniques used to assess the material properties of the films included AFM, EELS, RBS/ERDA, spectroscopic, electrical, stress, microhardness, and adhesion. These were correlated to the tribological performance of the coatings using wear measurements. The most important observation is that He dilution (>90%) promotes enhanced adhesion with respect to all substrate material studies. Coatings typically exhibit a microhardness of the order of 10-20 GPa in films 0.1microhardness, and adhesion. These were correlated to the tribological performance of the coatings using wear measurements. The most important observation is that He dilution (>90%) promotes enhanced adhesion with respect to all substrate materials studied. Coatings typically exhibit a microhardness of the order of 10-20 GPa in films 0.1 < d < 2 μm thick, with associated electrical resistivity in the range 108 < ρ < 1012 Ω·cm, coefficient of friction <0.1 and surface RMS roughness as low as 2 A. The results are discussed with respect to surface pre-treatment, ion surface bombardment, interfacial reactivity and changes in plasma gas breakdown processes.

Performance comparison of Stellite 6® deposited on steel using supersonic laser deposition and laser cladding

Stellite 6® powders were deposited on carbon steel using Supersonic Laser Deposition. The microstructure and performance of the coatings were examined using SEM, optical microscopy, EDS, XRD, microhardness testing and pin-on-disc wear testing. The results showed that the microstructure and wear behaviour of the most successful SLD deposition conditions with N2 at a pressure of 30bar, a temperature of 450°C and a deposition power of 1.5kW were compared with that of optimised laser cladding. © 2012 Elsevier B.V.