Laser microstructuring of Si surfaces for low-threshold field-electron emission

Dense arrays of high aspect ratio Si micro-pyramids have been formed by cumulative high intensity laser irradiation of doped Si wafers in an SF6 environment. A comparative study using nanosecond (XeCl, 308 nm) and femtosecond (Ti: Sapphire, 800 nm and KrF, 248 nm) laser pulses has been performed in this work. The influence of pulse duration and ambient gas pressure (SF6) is also presented. Scanning electron microscopy has shown that upon laser irradiation conical features appear on the Si surface in a rather homogenous distribution and with a spontaneous self alignment into arrays. Their lowest tip diameter is 800 nm; while their height reaches up to 90 mum. Secondary tip decoration appears on the surface of the formed spikes. Areas of 2 X 2 mm(2) covered with Si cones have been tested as cold cathode field emitters. After several conditioning cycles, the field emission threshold for the studied Si tips is as low as 2 V/mum, with an emission current of 10(-3) A/cm(2) at 4 V/mum. Even though these structures have smaller aspect ratios than good quality carbon nanotubes, their field emission properties are similar. The simple and direct formation of field emission Si arrays over small pre-selected areas by laser irradiation could lead to a novel approach for the development of electron sources. (C) 2003 Elsevier B.V. All rights reserved.

Gas-phase production of gold-decorated silica nanoparticles.

Gold-decorated silica nanoparticles were synthesized in a two-step process in which silica nanoparticles were produced by chemical vapor synthesis using tetraethylorthosilicate (TEOS) and subsequently decorated using two different gas-phase evaporative techniques. Both evaporative processes resulted in gold decoration of the silica particles. This study compares the mechanisms of particle decoration for a production method in which the gas and particles remain cool to a method in which the entire aerosol is heated. Results of transmission electron microscopy and visible spectroscopy studies indicate that both methods produce particles with similar morphologies and nearly identical absorption spectra, with peak absorption at 500-550 nm. A study of the thermal stability of the particles using heated-TEM indicates that the gold decoration on the particle surface remains stable at temperatures below 900 °C, above which the gold decoration begins to both evaporate and coalesce.

Self-assembled artificial pinning centres in thick YBCO superconducting films

Strong, artificial pinning centres are required in superconducting films of large thickness for power applications in high magnetic fields. One of the methods for the introduction of pinning centres in such films is substrate decoration, i.e., growing nanoscale islands of certain materials on the substrate prior to the deposition of the superconducting film. Two other methods are building up a layered distribution of a second phase and homogeneous incorporation of second phase inclusions from a compositional target. In this paper, we compare the effectiveness of these methods in terms of the type of the self-assembly of nanoparticles. The comparison is made over a large set of YBa2Cu3O7 films of thickness up to 6.6 μm deposited with Au, Ag, Pd, LaNiO3, PrBa2Cu 3O7, YBCO, BaZrO3 and Gd2Ba 4CuWOy nanoparticles. It is found that substrate-decoration self-assembly is able to provide higher critical current in low magnetic field than the incorporation of homogeneous second phase in the sample microstructure. By specific modification of substrate decoration we achieved the self-field critical current per centimetre of width of 896 A/cm at 77.3 K and 1620 A/cm at 65 K in a film of thickness of 4.8 μm. © 2010 IOP Publishing Ltd.