ANNEALING BEHAVIOUR OF HIGH DOSE As** plus IMPLANTS.

The annealing behaviour of doses up to 4. 10**1**6 ions/cm**2 implanted at ion currents up to 10ma is described. Differences between rapid isothermal and furnace annealing in the measured sheet resistances are due to different amounts of diffusion and to loss of dopant by evaporation. Implantation at high currents (10ma) does not appear to affect the quality of the regrown material provided the temperature rise during implantation is small.

TECHNIQUES FOR PRODUCING DEFECT-FREE SOI BY DUAL ELECTRON BEAM HEATING OF DEPOSITED POLYSILICON.

Advances in the dual electron-beam recrystallization technique arising from the fast scanning of a line beam parallel to the edges of narrow seeding windows are described. The resultant recrystallized layers are essentially defect-free, have good surface flatness, and cover large areas.