Stabilization of a complex perovskite superstructure under ambient conditions: Influence of cation composition and ordering, and evaluation as an SOFC cathode

Ba1.6Ca2.3Y1.1Fe5O13 is an Fe3+ oxide adopting a complex perovskite superstructure, which is an ordered intergrowth between the Ca2Fe2O5 and YBa2Fe3O8 structures featuring octahedral, square pyramidal, and tetrahedral B sites and three distinct A site environments. The distribution of A site cations was evaluated by combined neutron and X-ray powder diffraction. Consistent with the Fe3+ charge state, the material is an antiferromagnetic insulator with a Néel temperature of 480-485 °C and has a relatively low d.c. conductivity of 2.06 S cm-1 at 700 °C. The observed area specific resistance in symmetrical cell cathodes with the samarium-doped ceria electrolyte is 0.87 Ω cm2 at 700 °C, consistent with the square pyramidal Fe3+ layer favoring oxide ion formation and mobility in the oxygen reduction reaction. Density functional theory calculations reveal factors favoring the observed cation ordering and its influence on the electronic structure, in particular the frontier occupied and unoccupied electronic states. © 2010 American Chemical Society.

A resonant micromachined electrostatic charge sensor

A micromachined electrometer, based on the concept of a variable capacitor, has been designed, modeled, fabricated, and tested. The device presented in this paper functions as a modulated variable capacitor, wherein a dc charge to be measured is up-modulated and converted to an ac voltage output, thus improving the signal-to-noise ratio. The device was fabricated in a commercial standard SOI micromachining process without the need for any additional processing steps. The electrometer was tested in both air and vacuum at room temperature. In air, it has a charge-to-voltage conversion gain of 2.06 nV/e, and a measured charge noise floor of 52.4 e/rtHz. To reduce the effects of input leakage current, an electrically isolated capacitor has been introduced between the variable capacitor and input to sensor electronics. Methods to improve the sensitivity and resolution are suggested while the long-term stability of these sensors is modeled and discussed. © 2006 IEEE.

Controlling magnetic ordering in coupled nanomagnet arrays

We have fabricated using high-resolution electron beam lithography circular magnetic particles (nanomagnets) of diameter 60 nm and thickness 7 nm out of the common magnetic alloy supermalloy. The nanomagnets were arranged on rectangular lattices of different periods. A high-sensitivity magneto-optical method was used to measure the magnetic properties of each lattice. We show experimentally how the magnetic properties of a lattice of nanomagnets can be profoundly changed by the magnetostatic interactions between nanomagnets within the lattice. We find that simply reducing the lattice spacing in one direction from 180 nm down to 80 nm (leaving a gap of only 20 nm between edges) causes the lattice to change from a magnetically disordered state to an ordered state. The change in state is accompanied by a peak in the magnetic susceptibility. We show that this is analogous to the paramagnetic-ferromagnetic phase transition which occurs in conventional magnetic materials, although low-dimensionality and kinetic effects must also be considered.