12 resultados para COBALT DISILICIDE
em Cambridge University Engineering Department Publications Database
Resumo:
We used a cyclic reactive ion etching (RIE) process to increase the Co catalyst density on a cobalt disilicide (CoSi2) substrate for carbon nanotube (CNT) growth. Each cycle of catalyst formation consists of a room temperature RIE step and an annealing step at 450 °C. The RIE step transfers the top-surface of CoSi2 into cobalt fluoride; while the annealing reduces the fluoride into metallic Co nanoparticles. We have optimized this cyclic RIE process and determined that the catalyst density can be doubled in three cycles, resulting in a final CNT shell density of 6.6 × 10 11 walls·cm-2. This work demonstrates a very effective approach to increase the CNT density grown directly on silicides. © 2014 AIP Publishing LLC.
Resumo:
We have for the first time developed a self-aligned metal catalyst formation process using fully CMOS (complementary metal-oxide-semiconductor) compatible materials and techniques, for the synthesis of aligned carbon nanotubes (CNTs). By employing an electrically conductive cobalt disilicide (CoSi 2) layer as the starting material, a reactive ion etch (RIE) treatment and a hydrogen reduction step are used to transform the CoSi 2 surface into cobalt (Co) nanoparticles that are active to catalyze aligned CNT growth. Ohmic contacts between the conductive substrate and the CNTs are obtained. The process developed in this study can be applied to form metal nanoparticles in regions that cannot be patterned using conventional catalyst deposition methods, for example at the bottom of deep holes or on vertical surfaces. This catalyst formation method is crucially important for the fabrication of vertical and horizontal interconnect devices based on CNTs. © 2012 American Institute of Physics.
Resumo:
The construction of protein-based photoelectrochemical cells that produce a variety of alternating currents in response to discontinuous illumination is reported. The photovoltaic component is a protein complex from the purple photosynthetic bacterium Rhodobacter sphaeroides which catalyses photochemical charge separation with a high quantum yield. Photoelectrochemical cells formed from this protein, a mobile redox mediator and a counter electrode formed from cobalt disilicide, titanium nitride, platinum, or multi-walled carbon nanotubes (MWCNT) generate a direct current during continuous illumination and an alternating current with different characteristics during discontinuous illumination. In particular, the use of superhydrophobic MWCNT as the back electrode results in a near symmetrical forward and reverse current upon light on and light off, respectively. The symmetry of the AC output of these cells is correlated with the wettability of the counter electrode. Potential applications of a hybrid biological/synthetic solar cell capable of generating an approximately symmetrical alternating current are discussed. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Resumo:
One of the commonly used resins for immobilized metal affinity purification of polyhistidine-tagged recombinant proteins is TALON resin, a cobalt (II)--carboxymethylaspartate-based matrix linked to Sepharose CL-6B. Here, we show that TALON resin efficiently purifies the native form of Lac repressor, which represents the major contaminant when (His)(6)-tagged proteins are isolated from Escherichia coli host cells carrying the lacI(q) gene. Inspection of the crystal structure of the repressor suggests that three His residues (residues 163, 173, and 202) in each subunit of the tetramer are optimally spaced on an exposed face of the protein to allow interaction with Co(II). In addition to establishing a more efficient procedure for purification of the Lac repressor, these studies indicate that non-lacI(q)-based expression systems yield significantly purer preparations of recombinant polyhistidine-tagged proteins.
Resumo:
In the design of high-speed low-power electrical generators for unmanned aircraft and spacecraft, maximization of specific output (power/weight) is of prime importance. Several magnetic circuit configurations (radial-field, axial-field, flux-squeezing, homopolar) have been proposed, and in this paper the relative merits of these configurations are subjected to a quantitative investigation over the speed range 10 000–100000 rev/min and power range 250 W-10 kW. The advantages of incorporating new high energy-density magnetic materials are described. Part I deals with establishing an equivalent circuit for permanent-magnet generators. For each configuration the equivalent circuit parameters are related to the physical dimensions of the generator components and an optimization procedure produces a minimum volume design at discrete output powers and operating speeds. The technique is illustrated by a quantitative comparison of the specific outputs of conventional radial-field generators with samarium cobalt and alnico magnets. In Part II the specific outputs of conventional, flux-squeezing, and claw-rotor magnetic circuit configurations are compared. The flux-squeezing configuration is shown to produce the highest specific output for small sizes whereas the conventional configuration is best at large sizes. For all sizes the claw-rotor configuration is significantly inferior. In Part III the power densities available from axial-field and flux-switching magnetic circuit configurations are maximized, over the power range 0.25-10 kW and speed range 10 000–100000 rpm, and compared to the results of Parts I & II. For the axial-field configuration the power density is always less than that of the conventional and flux-squeezing radial-field configurations. For the flux-switching generator, which is able to withstand relatively high mechanical forces in the rotor, the power density is again inferior to the radial-field types, but the difference is less apparent for small (low power, high speed) generator sizes. From the combined results it can be concluded that the flux-squeezing and conventional radial-field magnetic circuit configurations yield designs with minimum volume over the power and speed ranges considered. © 1985, IEEE. All rights reserved.
Resumo:
Vertically-aligned carbon nanotubes (VA-CNTs) were rapidly grown from ethanol and their chemistry has been studied using a "cold-gas" chemical vapor deposition (CVD) method. Ethanol vapor was preheated in a furnace, cooled down and then flowed over cobalt catalysts upon ribbon-shaped substrates at 800 °C, while keeping the gas unheated. CNTs were obtained from ethanol on a sub-micrometer scale without preheating, but on a millimeter scale with preheating at 1000 °C. Acetylene was predicted to be the direct precursor by gas chromatography and gas-phase kinetic simulation, and actually led to millimeter-tall VA-CNTs without preheating when fed with hydrogen and water. There was, however a difference in CNT structure, i.e. mainly few-wall tubes from pyrolyzed ethanol and mainly single-wall tubes for unheated acetylene, and the by-products from ethanol pyrolysis possibly caused this difference. The "cold-gas" CVD, in which the gas-phase and catalytic reactions are separately controlled, allowed us to further understand CNT growth. © 2012 Elsevier Ltd. All rights reserved.
Resumo:
We show that catalyst pretreatment conditions can have a profound effect on the chiral distribution in single-walled carbon nanotube chemical vapor deposition. Using a SiO2-supported cobalt model catalyst and pretreatment in NH3, we obtain a comparably narrowed chiral distribution with a downshifted tube diameter range, independent of the hydrocarbon source. Our findings demonstrate that the state of the catalyst at the point of carbon nanotube nucleation is of fundamental importance for chiral control, thus identifying the pretreatment atmosphere as a key parameter for control of diameter and chirality distributions. © 2014 American Chemical Society.