Bundles of polytwins as meta-elastic domains in the thin polycrystalline simple multi-ferroic system PZT.

We used enhanced piezo-response force microscopy (E-PFM) to investigate both ferroelastic and ferroelectric nanodomains in thin films of the simple multi-ferroic system PbZr(0.3)Ti(0.7)O(3) (PZT). We show how the grains are organized into a new type of elastic domain bundles of the well-known periodic elastic twins. Here we present these bundle domains and discuss their stability and origin. Moreover, we show that they can arrange in such a way as to release strain in a more effective way than simple twinning. Finally, we show that these bundle domains can arrange to form the macroscopic ferroelectric domains that constitute the basis of ferroelectric-based memory devices.

Field emission properties of single-walled carbon nanotubes with a variety of emitter morphologies

Field emission properties of single-walled carbon nanotubes (SWCNTs), which were prepared through alcohol catalytic chemical vapor deposition for 10-60s, were characterized in a diode configuration. Protrusive bundles at the top surface of samples act selectively as emission sites. The number of emission sites was controlled by emitter morphologies combined with texturing of Si substrates. SWCNTs grown on a textured Si substrate exhibited a turn-on field as low as 2.4 V/μm at a field emission current density of 1 μA/cm 2. Uniform spatial luminescence (0.5 cm2) from the rear surface of the anode was revealed for SWCNTs prepared on the textured Si substrate. Deterioration of field emission properties through repetitive measurements was reduced for the textured samples in comparison with vertically aligned SWCNTs and a random network of SWCNTs prepared on flat Si substrates. Emitter morphology resulting in improved field emission properties is a crucial factor for the fabrication of SWCNT-electron sources. Morphologically controlled SWCNTs with promising emitter performance are expected to be practical electron sources. © 2008 The Japan Society of Applied Physics.