Durability study of eleven years old cement-bentonite cut-off wall material

Comprehensive understanding of the long-term performance of cement-bentonite slurry trench cut-off walls is essential as these mixes may degrade when exposed to aggressive environments or when subjected to prolonged drying. A series of wetting-drying and immersion experiments was carried out to evaluate the durability characteristics of laboratory mixed samples and block field samples from 40 days to 11 years of age. For the wetting-drying tests, the samples buried in medium graded sand were subjected to periodical flooding and drying cycles. They were then used for permeability testing and unconfined compressive strength (UCS) testing. For the immersion tests, the samples confined in perforated molds were submerged in magnesium sulfate solution for 16 weeks and their microstructures were then analyzed using X-ray diffraction (XRD) technique. This paper identifies the effects of contaminant exposure on durability of cement-bentonite and the effects of aging by comparing 11 years old samples to younger samples. Test results showed that young or previously contaminated cement-bentonite mixes are more susceptible to sulfate attack than old or less contaminated mixes. Copyright ASCE 2008.

Long-term performance of cement-bentonite containment wall

The paper presents hydraulic conductivity, unconfined compression strength (UCS) and triaxial test results of an 11 year old slag-cement-bentonite (CB) cut-off wall material and identifies factors affecting their long-term performance. The laboratory tests were performed on three types of CB samples ranging from contaminated block field samples to uncontaminated laboratory cast samples. The results showed that hydraulic conductivity reduces till 3 years and UCS increases till 90 days, but there after it remains constant till 11 years of age. The mean hydraulic conductivity and UCS values of block field samples are inferior and have large variability than laboratory cured samples. Such variations are mainly because of heterogeneity caused by aggressive environment and impurities within the specimen. Consolidated undrained triaxial test found that under an effective confining pressure of less than 200 kPa, tension failure occurred since the minor principal stress dropped to zero value at failure. The research outcome is useful for understanding future liability of CB wall and improving their design. © 2009 IOS Press.

Cement bentonite cutoff walls for polluted sites

Cement-bentonite (CB) cutoff walls have long been used to control ground water flow and contaminant migration at polluted sites. Hydraulic conductivity and unconfined compressive strength are two short-term properties often used by industry and owners in CB specification and are important parameters discussed in this paper. For polluted sites, long-term compatibility is also an important issue. These properties are coupled to a number of external factors including the mix design, construction sequence, presence/absence of contaminants at the site. Additional short-term properties for engineering assessment include the stressstrain characteristics in both drained and undrained shear in both with and without confinement as well as one-dimensional consolidation properties. Long term CB properties are affected by aging, reaction chemistry, drying, in situ stress state, and interaction with the polluted environment. © 2013 Taylor & Francis Group.

The effect of cationic, non-ionic and amphiphilic surfactants on the intercalation of bentonite

Surfactant-clay interactions are key for the development of new clay applications and inorganic-organic nanocomposites. Bentonite, with montmorillonite as the principal clay mineral constituent, was modified with varying concentrations of hexadecethyltrimethylammonium chloride (HDTMA), as a reference cationic surfactant, polypropylene glycol (PPG) 1200 and 2000, as non-ionic surfactants, and lecithin and Topcithin®, as amphiphilic phospholipid surfactants, according to the cation exchange capacity (CEC). The modified bentonites were characterised by X-ray diffraction, thermogravimetric analysis (TGA), Fourier transform infrared (FTIR) spectrometry, specific surface area and pore volume. Three intercalation regions have been identified depending on the surfactant. The non-ionic surfactant caused only a crystalline expansion of bentonite interlayers, while the cationic surfactant induced an osmotic intercalation. The amphiphilic lecithin derivatives intercalated more extensively with the bentonite matrix. The TGA and the FTIR spectra showed that, at lower concentrations, the PPGs and HDTMA adopted a disordered conformation that required more energy to degrade, while at higher concentrations, the surfactants were ordered in the interlayer space of the bentonite. The lecithin derivative surfactant had a greater thermal and conformation stability. The specific surface area reduced with increasing surfactant concentrations. This study highlights the effect of surfactant type on the interlayer space of montmorillonite in the perspective of developing novel clay functions. © 2013.

Comparison between granular pillared, organo- and inorgano-organo-bentonites for hydrocarbon and metal ion adsorption

Granular reactive materials have higher permeability and are therefore desirable for in situ groundwater pollution control. Three granular bentonites were prepared: an Al-pillared bentonite (PBg), an organo-bentonite (OBg) using a quaternary ammonium cation (QAC), and an inorgano-organo-bentonite (IOBg), using both the pillaring agent and the QAC. Powdered IOB (IOBp) was also prepared to test the effect of particle size. The modified bentonites were characterised with X-ray diffraction (XRD), Fourier transform infrared spectrometry (FT-IR), thermal gravimetric analysis (TGA) and uniaxial compression tests. The d-spacing increased only with QAC intercalation. The Young's modulus of IOBg was twice as high as OBg. Batch adsorption tests were performed with aqueous multimetal solutions of Pb2+, Cu2+, Cd2+, Zn2+ and Ni2+ ions, with liquid dodecane and with aqueous dodecane solutions. Metal adsorption fit the Langmuir isotherm. Adsorption occurred within 30min for PBg, while the granular organo-bentonite needed at least 12h to reach equilibrium. IOBp had the maximum adsorption capacity at higher metal concentration and lower adsorbent content (Cu2+: 2.2, Ni2+: 1.7, Zn2+: 1.4, Cd2+: 0.9 and Pb2+: 0.7 all in mmolg-1). The dual pillaring of the QAC and Al hydroxide increased the adsorption. The adsorption of liquid dodecane was in the order IOBg>OBg>PBg (3.2>2.7>1.7mmolg-1). Therefore IOBg has potential for the removal of toxic compounds found in soil, groundwater, storm water and wastewater. © 2012 Elsevier B.V.

The efficiency of compensation grouting in sands

Physical model experiments on compensation grouting in sands were performed in two different setups (Cambridge and Delft). The effect of water-cement (w/c) ratio, bentonite content (b.c.) and injection rate on compensation efficiency was investigated. Results show a considerable drop in compensation efficiency resulted from reducing the soil density. Injection in dense sand (R.D. = 93%) resulted in efficiencies between 40-90%, whereas injection in medium-dense sand (R.D. = 60-75%) yielded in reduced efficiencies between 10-40%. When the w/c ratio increased from 0.5 to 1.5 for a given density (R.D. = 93%) and the b.c. of 4%, the compensation efficiency value decreased. Typical efficiencies were between 60% and 40-50% for w/c ratios of 0.5 and 1.5, respectively. The values of compensation and grout efficiencies were almost equal, suggesting that pressure filtration happens mainly during injection. Increasing the b.c. improved the compensation efficiency. When a higher b.c. of 12% to 14% was used, typical compensation efficiencies in dense sand were 78 and 90% for w/c ratios of 1.5 and 1.8 respectively. © 2012 Taylor & Francis Group.

Influence of Peripheral Velocity on Vane Shear Strength of an Artificial Clay

Shearing rate is among the most important factors affecting the undrained shear strength of clays. In particular, for seismic or storm-wave loading conditions, the shearing rate is much higher than that used in many common laboratory or field tests. The testing program described here evaluates the effect of peripheral velocity on the undrained strength inferred from the shear vane test. The study was conducted on a lightly cemented bentonite-kaolinite mixture manufactured in the laboratory, which possesses many characteristics similar to those of natural materials. Results show that the shear strength increases with increasing peripheral velocity, while the residual shear strength seems to be nearly independent of rotation rate.