The high-field properties of polycrystalline superconducting TlBaCaCuO films fabricated by the incorporation of thallium vapour into air-atomised BaCaCuO precursors are described. Thick films with Tc values in the range 106-111 K have been prepared on polycrystalline yttria-stabilised zirconia substrates. The surface morphology, crystal structure and composition of the films are related to their high-field transport and magnetisation properties. Typical 10 mm × 9 mm films show Jc values > 1×104 A/cm2 at 77 K (0 T). The best film has a Jc=1.3×104 A/cm2 (Ic=3.6 A) at 77 K (0 T). Films prepared on 26 mm×9 mm substrates show typical large-area Jc values > 0.5×104 A/cm2 (77 K, 0 T). A square planar specimen of dimensions 4.3 mm ×4.3 mm exhibited magnetisation Jc values=1.2×105 A/cm2 at 4.2 K (0.1 T), 9.3×104 A/cm2 at 10 K (0.1 T), 3.3×104 A/ cm2 at 4 K (8 T), and 1.6×104 A/cm2 at 10 K (8 T). © 1994.

Development of non-weak link bulk YBCO grain boundaries for high magnetic field eegimeering applications

A non-weak link joining technique has been developed for YBCO pseudo-crystals fabricated by seeded peritectic solidification based on the formation of a liquid phase which segregates from the platelet boundaries at temperatures above = 920 °C. Electrical and magnetic measurements on these boundaries suggest that their irreversibility field can be as high as 7 T at 77 K in fully oxygenated pseudo-crystals joined along their crystallographic ab-planes which is comparable to the irreversibility behaviour of the adjacent YBCO grains. © 1999 IEEE.