Innovative fabrication of PZT pillar arrays by a colloidal approach

An innovative approach for fabricating pillar arrays for ultrasonic transducer applications is disclosed. It involves the preparation of concentrated piezoelectric lead zirconate titanate (PZT) suspensions in aqueous solutions of epoxy resin and its polymerization upon adding a polyamine based hardener. Zeta potential and rheological measurements revealed that 1wt.% dispersant, 20wt.% of epoxy resin and a hardener/epoxy resin ratio of 0.275mLg -1, were the optimized contents to obtain strong PZT samples with high green strength (35.21±0.39MPa). Excellent ellipsoidal and semi-circle shaped pillar arrays presenting lateral dimensions lower than 10μm and 100μm height were successfully achieved. The organics burning off was conducted at 500°C for 2h at a heating rate of 1°Cmin -1. Sintering was then carried out in the same heating cycle at 1200°C for 1h. The microstructures of the green and sintered ceramics were homogeneous and no large defects could be detected. © 2011 Elsevier Ltd.

Optical and structural properties of Er2O3 films grown by magnetron sputtering

The structural properties and the room temperature luminescence of Er 2O3 thin films deposited by magnetron sputtering have been studied. In spite of the well-known high reactivity of rare earth oxides towards silicon, films characterized by good morphological properties have been obtained by using a SiO2 interlayer between the film and the silicon substrate. The evolution of the properties of the Er2O3 films due to thermal annealing processes in oxygen ambient performed at temperatures in the range of 800-1200°C has been investigated in detail. The existence of well defined annealing conditions (rapid treatments at a temperature of 1100°C or higher) allowing to avoid the occurrence of extensive chemical reactions with the oxidized substrate has been demonstrated; under these conditions, the thermal process has a beneficial effect on both structural and optical properties of the film, and an increase of the photoluminescence (PL) intensity by about a factor of 40 with respect to the as-deposited material has been observed. The enhanced efficiency of the photon emission process has been correlated with the longer lifetime of the PL signal. Finally, the conditions leading to a reaction of Er2O3 with the substrate have been also identified, and evidences about the formation of silicate-like phases have been collected. © 2006 American Institute of Physics.