Hardfacing using supersonic laser depostion of stellite-6

The capability of manufacturing coatings is of central importance in engineering design. Many components require nowadays the application of additional layers, to enhance mechanical properties and protect against hostile environments. Supersonic Laser Deposition (SLD) is a novel coating method, based upon Cold Spray (CS) principles. In this technique the deposition velocities can be significantly lower than those required for effective bonding in CS applications. The addition of laser heat energy permits a change in the thermodynamic experience of impacting particles, thereby offering a greater opportunity for metallurgical bonding at lower velocities compared to the CS process technology. The work reported in this paper demonstrates the ability of the SLD process to deliver hard facing materials to engineering surfaces. Stellite-6 has been deposited on low carbon steel tubes over a range of process parameters, determining the appropriate target power and traverse speeds for coating deposition. Coating properties and parameters were examined to determine the main properties, micro-structure and processing cost. Their morphology was studied through optical microscopy, SEM and X-Ray Diffraction. The results have shown that SLD is capable of depositing Stellite-6, with enhanced properties compared to laser clad counterparts.

Effect of laser heating temperature on coating characteristics of Stellite 6 deposited by cold spray

Laser-assisted cold spray (LCS) is a new coating and fabrication process which combines some advantages of CS: solid-state deposition, retain their initial composition and high build rate with the ability to deposit materials which are either difficult or impossible to deposit using cold spray alone. Stellite 6 powder is deposited on medium carbon steels by LCS using N 2 as carrier gas pressure. The topography, cross section thickness, structure of the coatings is examined by SEM, optical microscopy, EDX. The results show that thickness and fluctuation of coating are improved with increased deposition site temperature. Porosity of coating is affected by N 2 and deposition site temperature. In this paper, it presents optimal coating using N 2 at a pressure of 3 MPa and temperature of 450°C and deposition site temperature of 1100°C.