Failure mechanisms and toughness of Al2O3 ductile-particle toughened ceramics and SiC fibre-ceramic composites

The development of high performance ceramics and ceramic composites often relies on assumptions about their behaviour during loading and at failure. A crucial influence on the mechanical properties of these materials is the degree of sub-critical cracking, which post mortem investigations cannot adequately reveal. Hence a clear picture of the dynamic micromechanisms of cracking is required if applications of fracture and damage mechanics to theoretical models is to be meaningful.

Resonance phenomena in a ferroelectric liquid crystals

In a surface stabilized ferroelectric liquid crystal cell, optical transmission oscillations have been revealed accompanying mechanical vibrations caused by fast field reversal. Special bookshelf textures, so-called "rainbow", were used in the experiments. Temperature dependences of the oscillation parameters have been studied. The temperature dependence of the oscillation frequency suggests that the some oscillation resonances correspond to modes of the liquid crystals.

A comparison of different failure assessment methodologies applied to the NESC-1 test

Predictions for a 75x205mm surface semi-elliptic defect in the NESC-1 spinning cylinder test have been made using BS PD 6493:1991, the R6 procedure, non-linear cracked body finite element analysis techniques and the local approach to fracture. All the techniques agree in predicting ductile tearing near the inner surface of the cylinder followed by cleavage initiation. However they differ in the amount of ductile tearing, and the exact location and time of any cleavage event. The amount of ductile tearing decreases with increasing sophistication in the analysis, due to the drop in peak crack driving force and more explicit consideration of constraint effects. The local approach predicts a high probability of cleavage in both HAZ and base material after 190s, while the other predictions suggest that cleavage is unlikely in the HAZ due to constraint loss, but likely in the underlying base material. The timing of this event varies from ∼150s for R6 predictions to ∼250-300s using non-linear cracked body analysis.