Fabrication of large grain Nd-Ba-Cu-O by seeded melt growth

Large, single grain Nd-Ba-Cu-O (NdBCO) composite samples of NdBa2Cu3O7-δ (Nd-123) containing 15 and 20 mol. % non-superconducting Nd4Ba2Cu2O10 (Nd-422) phase inclusions have been fabricated successfully by a variety of techniques based on top-seeded melt growth under reduced oxygen partial pressure. Specifically, individual grains up to 2cm in diameter have been grown using (100) oriented MgO seeding, self (NdBCO) seeding at elevated temperature and self-seeding of Ag and Au doped precursor pellets. The latter exhibit a reduced peritectic decomposition temperature compared with the undoped compound. These techniques, which vary in degree of difficulty and hence reliability, yield grains with a range of microstructural homogeneity. This paper describes the general aspects of large NdBCO grain fabrication and presents the results of the different fabrication techniques.

Effect of size, morphology and crystallinity of seed crystal on the nucleation and growth of single grain Y-Ba-Cu-O

The effect of size, morphology and crystallinity of seed crystals on the nucleation and growth of large grain Y-Ba-Cu-O (YBCO) bulk superconductors fabricated by top seeded melt growth (TSMG) has been investigated. Seeding bulk samples with small, square shaped seed crystals leads to point nucleation and growth of the superconducting YBa2Cu3O7-y (Y-123) phase that exhibits the usual square habitual growth symmetry. The use of triangular and circular shaped seed crystals, however, modifies significantly the growth habit geometry of the grain. The use of large area seeds both increases the rate of epitaxial nucleation of the Y-123 phase and produces relatively large crystals in the incongruent melt, which decreases significantly the processing times of large grain samples. The present study is relevant to decrease processing times of samples with both preferred or no growth sectors and for multiple seeding of large grain samples which contain clean grain boundaries. © 2005 Published by Elsevier Ltd.

Large single grain (RE)-Ba-Cu-O superconductors with nano-phase inclusions

Nano-phase (5-20 nm) particles of YBa2(Cu0.5M 0.6)O6 [where M = Nb, Ta, Mo, W, Zr and Hf] have been introduced successfully into RE-Ba-Cu-O single grain superconductors. A study to enlarge the size of a single grain containing these particles has been carried out involving measurement of the growth rate as a function of YBa 2(Cu0.5M0.6)O6 phase concentration and degree of un-dercooling. The influence of the change in YBa2 (Cu0.8M0.5)O6 concentration on microstructural features is also investigated and the superconducting properties of these large grain superconductors are presented. © 2005 IEEE.

Superconducting properties of Gd-Ba-Cu-O single grains processed from a new, Ba-rich precursor compound

Gd-Ba-Cu-O (GdBCO) single grains have been previously melt-processed successfully in air using a generic Mg-Nd-Ba-Cu-O (Mg-NdBCO) seed crystal. Previous research has revealed that the addition of a small amount of BaO 2 to the precursor powders prior to melt processing can suppress the formation of Gd/Ba solid solution, and lead to a significant improvement in superconducting properties of the single grains. Research into the effects of a higher Ba content on single grain growth, however, has been limited by the relatively small grain size in the earlier studies. This has been addressed by developing Ba-rich precursor compounds Gd-163 and Gd-143, fabricated specifically to enable the presence of greater concentrations of Ba during the melt process. In this study, we propose a new processing route for the fabrication of high performance GdBCO single grain bulk superconductors in air by enriching the precursor powder with these new Ba rich compounds. The influence of the addition of the new compounds on the microstructures and superconducting properties of GdBCO single grains is reported. © 2008 IOP Publishing Ltd.

Microstructure and superconducting properties of single grains of Y-Ba-Cu-O containing Y-2411(M) and Y2O3

Y-Ba-Cu-O (YBCO) single grains have the potential to generate large trapped magnetic fields for engineering applications, and research on the processing and properties of this material has attracted interest world-wide over the past 20 years. In particular, the introduction of flux pinning centers to the large grain microstructure to improve its current density Jc, and hence trapped field, has been investigated extensively. Y2Ba 4CuMO2 [Y-2411(M)], where M = Nb, Ta, Mo, W, Ru, Zr, Bi and Ag, has been discovered recently to form very effective flux pinning centers due primarily to its ability to form nano-size inclusions in the superconducting phase matrix. However, the addition of the Y-2411(M) phase to the precursor composition complicates the melt-processing of single grains. The addition of Y2O3 to the precursor composition, however, broadens the growth window of single YBCO grains containing Y-2411 (M). We report an investigation of the microstructures and superconducting properties of single grains of this composition grown by top seeded melt growth (TSMG). © 2010 IEEE.

Calculating transport AC losses in stacks of high temperature superconductor coated conductors with magnetic substrates using FEM

In this paper, the authors investigate the electromagnetic properties of stacks of high temperature superconductor (HTS) coated conductors with a particular focus on calculating the total transport AC loss. The cross-section of superconducting cables and coils is often modeled as a two-dimensional stack of coated conductors, and these stacks can be used to estimate the AC loss of a practical device. This paper uses a symmetric two dimensional (2D) finite element model based on the H formulation, and a detailed investigation into the effects of a magnetic substrate on the transport AC loss of a stack is presented. The number of coated conductors in each stack is varied from 1 to 150, and three types of substrate are compared: non-magnetic weakly magnetic and strongly magnetic. The non-magnetic substrate model is comparable with results from existing models for the limiting cases of a single tape (Norris) and an infinite stack (Clem). The presence of a magnetic substrate increases the total AC loss of the stack, due to an increased localized magnetic flux density, and the stronger the magnetic material, the further the flux penetrates into the stack overall. The AC loss is calculated for certain tapes within the stack, and the differences and similarities between the losses throughout the stack are explained using the magnetic flux penetration and current density distributions in those tapes. The ferromagnetic loss of the substrate itself is found to be negligible in most cases, except for small magnitudes of current. Applying these findings to practical applications, where AC transport current is involved, superconducting coils should be wound where possible using coated conductors with a non-magnetic substrate to reduce the total AC loss in the coil. © 2011 Elsevier B.V. All rights reserved.

Simulation studies on the magnetization of (RE)BCO bulk superconductors using various split-coil arrangements

Simulation studies were conducted on the magnetization of (RE)BCO (RE-Ba-Cu-O, where RE represents a rare earth element) bulk superconductors using various split-coil arrangements by solving the critical state equation using the commercial software FlexPDE. A pair of coaxial coils of identical size is identified as an optimum arrangement for practical magnetization at 77K by the zero-field cooling technique. In general, the magnetization process is likely to be most effective when the outer radius of the coils lies between 100% and 50% of the sample radius. A relatively large coil pair is necessary for samples with either a smaller aspect ratio or larger values of J c0. Two different regimes of flux penetration are found to be involved in the magnetization process. For a sufficiently small sample, the penetration field is determined by flux propagation from beneath the coil to the centre of the sample; for a sufficiently large sample, the definitive propagation route is from beneath the coil to the periphery of the sample. Effective split-coil magnetization occurs only in the former regime, and both penetration regimes are completely different from that involved in the solenoidal-coil magnetization process. © 2012 IOP Publishing Ltd.

The parameter space of graphene chemical vapor deposition on polycrystalline Cu

A systematic study of the parameter space of graphene chemical vapor deposition (CVD) on polycrystalline Cu foils is presented, aiming at a more fundamental process rationale in particular regarding the choice of carbon precursor and mitigation of Cu sublimation. CH 4 as precursor requires H 2 dilution and temperatures ≥1000 °C to keep the Cu surface reduced and yield a high-quality, complete monolayer graphene coverage. The H 2 atmosphere etches as-grown graphene; hence, maintaining a balanced CH 4/H 2 ratio is critical. Such balance is more easily achieved at low-pressure conditions, at which however Cu sublimation reaches deleterious levels. In contrast, C 6H 6 as precursor requires no reactive diluent and consistently gives similar graphene quality at 100-150 °C lower temperatures. The lower process temperature and more robust processing conditions allow the problem of Cu sublimation to be effectively addressed. Graphene formation is not inherently self-limited to a monolayer for any of the precursors. Rather, the higher the supplied carbon chemical potential, the higher the likelihood of film inhomogeneity and primary and secondary multilayer graphene nucleation. For the latter, domain boundaries of the inherently polycrystalline CVD graphene offer pathways for a continued carbon supply to the catalyst. Graphene formation is significantly affected by the Cu crystallography; i.e., the evolution of microstructure and texture of the catalyst template form an integral part of the CVD process. © 2012 American Chemical Society.

Experimental studies of the quench behaviour of MgB2 superconducting wires for fault current limiter applications

Various MgB2 wires with different sheath materials provided by Hyper Tech Research Inc., have been tested in the superconducting fault current limiter (SFCL) desktop tester at 24-26K in a self-field. Samples 1 and 2 are similarly fabricated monofilamentary MgB2 wires with a sheath of CuNi, except that sample 2 is doped with SiC and Mg addition. Sample 3 is a CuNi sheathed multifilamentary wire with Cu stabilization and Mg addition. All the samples with Nb barriers have the same diameter of 0.83mm and superconducting fractions ranging from 15% to 27% of the total cross section. They were heat-treated at temperatures of 700 °C for a hold time of 20-40min. Current limiting properties of MgB2 wires subjected to pulse overcurrents have been experimentally investigated in an AC environment in the self-field at 50Hz. The quench currents extracted from the pulse measurements were in a range of 200-328A for different samples, corresponding to an average engineering critical current density (Je) of around 4.8 × 10 4Acm-2 at 25K in the self-field, based on the 1νVcm-1 criterion. This work is intended to compare the quench behaviour in the Nb-barrier monofilamentary and multifilamentary MgB2 wires with CuNi and Cu/CuNi sheaths. The experimental results can be applied to the design of fault current limiter applications based on MgB2 wires. © IOP Publishing Ltd.