Fracture energy of the concrete-FRP interface in strengthened beams

To determine the load at which FRPs debond from concrete beams using global-energy-balance-based fracture mechanics concepts, the single most important parameter is the fracture energy of the concrete-FRP interface, which is easy to define but difficult to determine. Debonding propagates in the narrow zone of concrete, between the FRP and the (tension) steel reinforcement bars in the beam, and the presence of nearby steel bars prevents the fracture process zone, which in concrete is normally extensive, from developing fully. The paper presents a detailed discussion of the mechanism of the FRP debonding, and shows that the initiation of debonding can be regarded as a Mode I (tensile) fracture in concrete, despite being loaded primarily in shear. It is shown that the incorporation of this fracture energy in the debonding model developed by the authors, details of which are presented elsewhere, gives predictions that match the test results reported in the literature. © 2013 Elsevier Ltd.

A computational fluid-structure interaction study of inflation cycles of a tension cone decelerator

Inflatable aerodynamic decelerators present potential advantages for planetary entry in missions of robotic and human exploration. The design of these structures face many engineering challenges, including complex deformable geometries, anisotropic material response, and coupled shockturbulence interactions. In this paper, we describe a comprehensive computational fluid-structure interaction study of an inflation cycle of a tension cone decelerator in supersonic flow and compare the simulations with earlier published experimental results. The aeroshell design and flow conditions closely match recent experiments conducted at Mach 2.5. The structural model is a 16-sided polygonal tension cone with seams between each segment. The computational model utilizes adaptive mesh refinement, large-eddy simulation, and shell mechanics with self-contact modeling to represent the flow and structure interaction. This study focuses on the dynamics of the structure as the inflation pressure varies gradually, and the behavior of forces experienced by the flexible and rigid (the payload capsule) structures. © 2011 by the American Institute of Aeronautics and Astronautics, Inc. All rights reserved.

Modeling mode i fracture of bitumen films

The fracture behavior of thin films of bitumen in double cantilever beam (DCB) specimens was investigated over a wide range of temperature and loading rate conditions using finite-element analysis. The model includes a phenomenological model for the mechanical behavior of bitumen, implemented into a special-purpose finite-element user material subroutine, combined with a cohesive zone model (CZM) for simulating the fracture process. The finite-element model is validated against experimental results from laboratory tests of DCB specimens by comparing measured and predicted load-line deflection histories and fracture energy release rates. Computer simulation results agreed well with experimental data of DCB joints containing bitumen films in terms of peak stress, fracture toughness, and stress-strain history response. The predicted "normalized toughness," G=2h, was found to increase in a power-law manner with effective temperaturecompensated strain rate in the ductile region as previously observed experimentally. In the brittle regime, G=2h is virtually constant. The model successfully captured the ductile and brittle failure behavior of bitumen films in opening mode (tension) for stable crack growth conditions. © 2013 American Society of Civil Engineers.

Conceptual transformation framework for servitization

This paper presents a Conceptual Transformation Framework for Servitization. The challenges experienced by manufacturers on their journey to servitization are investigated in order to develop our understanding of the transformation that traditional manufacturers undergo to become servitized manufacturers. Three change theories are applied to develop the Framework: Lewin's force field analysis, Senge's system thinking and Pettigrew and Whipp's framework of strategic change. The Framework includes the dimensions of the change that takes place and the elements of change when transforming towards Product-Service Systems.

Fracture mechanics of idealised bituminous mixes

© 2014 Taylor & Francis. The durability of asphalt pavements is strongly impaired by cracks, caused primarily by traffic loads and environmental effects. In this work, fracture behaviour of idealised asphalt mixes is investigated. Experiments on idealised asphalt mixes under pure-tension mode (mode I cracking) were performed and fracture parameters were evaluated. In these three-point bend fracture tests, the test variables were temperature and load rate. The test data were stored in an asphalt materials database and special-purpose tools were implemented to analyse and handle the laboratory data automatically. Fracture mechanism maps were constructed, showing the conditions associated with ductile, brittle and ductile-brittle transition regimes of behaviour. The mechanism maps show the failure response of the material in terms of the stress intensity factor, strain energy release rate and J-integral as a function of the temperature-compensated crack mouth opening strain rate. Fracture behaviour of asphalt mix specimens was simulated by cohesive zone model in conjunction with a novel material constitutive model for asphalt mixes. The finite element model agrees well with the experimental results and provides insights into fracture response of the notched asphalt mix beam specimens.