Crystal growth of melt-textured Nd-123 under 1% oxygen partial pressure atmosphere

Crystal growth of melt-textured Nd-123 pseudo-crystals was investigated via an isothermal solidification with top-seeding technique under a 1%O2 in N2 atmosphere. Non-steady state solidification was observed at low undercooling, in contrast to an almost linear growth at higher undercooling. Similar to processing in air, the substitution of Nd/Ba was found to decrease from the seed position to the edge of the crystal. In addition, the volume fraction of Nd-422 particles decreased in the solid as solidification proceeded. As a result of these microstructural inhomogeneities, the critical temperature and the critical current density varied within the crystal even for samples processed isothermally, despite the narrow solid solution range of the Nd-123 phase under a reduced pO2 atmosphere.

Magnetic field and current distributins in melt-textured YBa 2Cu 3O 7-x with an artificial grain boundary

Using a magneto-optical (MO) technique, magnetic field distributions have been measured in a melt-textured YBa 2Cu 3O 7-x bulk superconductor, joined to form an artificial grain boundary (GB), in an external magnetic field perpendicular to the sample surface. The magnetic field at a weak section of the GB shows different values between the field increasing up to 150mT and decreasing down to 0T after zero-field-cooling. Namely, the magnetic field in increasing field is higher than that in decreasing field, even in the same external field. This result supports a model in which such differences in magnetic field at the weak-link GB give rise to the hysteresis behavior in the field dependence of transport critical current density in polycrystalline samples. The field distributions across a well-joined region of the GB behave similarly to the adjoining bulk material and this result indicates the possibility of creating useful artifacts provided that the strongly coupled sections can be reproduced on a larger scale.

Behavior of bulk melt-textured YBCO single domains subjected to crossed magnetic fields

We have experimentally investigated the crossed magnetic field effects on bulk melt-processed YBCO single domains. The samples were first permanently magnetized along their c-axis and then subjected to several cycles of a transverse magnetic field parallel to the ab planes. The magnetic properties along the c and ab directions were simultaneously measured using a couple of orthogonal pick-up coils as well as a Hall probe placed against the sample surface. The effects of both sweep amplitude and polarity were investigated. Field sweeps of alternate polarities are shown to affect the decay of the c-axis magnetization much more strongly than field sweeps of unique polarity do. However, the c-axis magnetization does not show any saturation even after a large number of field sweeps. Next, a micro-Hall probe scanning system was used to measure the distribution of magnetic induction over the top surface of the single domain subjected to the same combination of magnetic fields. The results are shown to be consistent with those determined with the sensing coils and bring out the role played by geometric effects.

Fabrication of large grain Nd-Ba-Cu-O by seeded melt growth

Large, single grain Nd-Ba-Cu-O (NdBCO) composite samples of NdBa2Cu3O7-δ (Nd-123) containing 15 and 20 mol. % non-superconducting Nd4Ba2Cu2O10 (Nd-422) phase inclusions have been fabricated successfully by a variety of techniques based on top-seeded melt growth under reduced oxygen partial pressure. Specifically, individual grains up to 2cm in diameter have been grown using (100) oriented MgO seeding, self (NdBCO) seeding at elevated temperature and self-seeding of Ag and Au doped precursor pellets. The latter exhibit a reduced peritectic decomposition temperature compared with the undoped compound. These techniques, which vary in degree of difficulty and hence reliability, yield grains with a range of microstructural homogeneity. This paper describes the general aspects of large NdBCO grain fabrication and presents the results of the different fabrication techniques.

Grain boundaries in multi-seeded melt-grown superconductors

Future applications of high temperature superconductors require bulk materials of a complex shape. The multi-seeded-melt-growth process (MSMG) represents a promising technique for obtaining qualitatively well oriented bulk materials with different kinds of shape. In the MSMG process, several seeds are placed on a precursor pellet, from which the growth of the bulk starts. A certain problem of the MSMG process is that grain boundaries become inevitable when the growth fronts of two neighboring seeds collide. These grain boundaries are responsible for a reduction of the critical currents and pose a problem for high current applications. By polishing the sample step by step, the influence of the grain boundaries was investigated by scanning Hall probe measurements and by the magnetoscan technique. Additionally, optical microscopy and electron microscopy were employed to investigate the details of the microstructure. © 2005 IEEE.

Properties of grain boundaries in bulk, melt processed YB2Cu3O7-δ fabricated using bridge-shaped seeds

Single grain REBa2C3uO7 ((RE)BCO, where RE is a rare earth element or yttrium) bulk superconducting materials have significant potential for a variety of engineering applications due to their ability to trap high magnetic fields. However, it is well known that the presence of grain boundaries coupled with a high angle of misorientation (typically 5�) significantly reduces the critical current density, J c , in all forms of high temperature superconducting materials. It is of considerable fundamental and technological interest, therefore, to investigate the grain boundary properties of bulk, film and tape (RE)BCO. We report a successful multi-seeding technique for the fabrication of fully aligned, artificial (0��misalignment) grain boundaries within large grain YBCO bulk superconductors using bridge-shaped seeds. The microstructure and critical current densities of the grain boundaries produced by this technique have been studied in detail.