ANNEALING BEHAVIOUR OF HIGH DOSE As** plus IMPLANTS.

The annealing behaviour of doses up to 4. 10**1**6 ions/cm**2 implanted at ion currents up to 10ma is described. Differences between rapid isothermal and furnace annealing in the measured sheet resistances are due to different amounts of diffusion and to loss of dopant by evaporation. Implantation at high currents (10ma) does not appear to affect the quality of the regrown material provided the temperature rise during implantation is small.

TIME RESOLVED REFLECTIVITY MEASUREMENTS APPLIED TO RAPID ISOTHERMAL ANNEALING OF ION IMPLANTED SILICON.

The annealing of ion implantation damage in silicon by rapid isothermal heating has been monitored by the time resolved reflectivity (TRR) method. This technique was applied simultaneously at a wavelength of 632. 8nm and also at 1152nm, where the optical absorption coefficient of silicon is less. The two wavelength method simplifies the interpretation of TRR results, extends the measurement depth and allows good resolution of the position of the interface between amorphous and crystalline silicon. The regrowth of amorphous layers in silicon, created by self implantation and implanted with electrically active impurities, was observed. Regrowth in rapid isothermal annealing occurs during the heating up stage of typical thermal cycles. Impurities such as B, P, and As increase the regrowth rate in a manner consistent with a vacancy model for regrowth. The maximum regrowth rate in boron implanted silicon is limited by the solid solubility.

COMPARISON OF MILLISECOND ANNEALING OF B IMPLANTS AND ISOTHERMAL ANNEALING FOR TIMES OF A FEW SECONDS.

The annealing behaviour of B implants in the millisecond time regime using a combination of swept line beam and background heating is compared with isothermal annealing with heating cycles of a few seconds. Carrier concentration profiles show that under annealing conditions which restrict diffusion, millisecond processing gives higher activation of B implants than isothermal heating. Transmission electron microscopy shows that millisecond annealing also results in a lower defect density.

RESIDUAL DEFECTS FOLLOWING RAPID ANNEALING OF BORON IMPLANTED SILICON WITH AND WITHOUT PREAMORPHISATION BY SILICON IMPLANTATION.

Implants of boron into silicon which has been made amorphous by silicon implantation have a shallower depth profile than the same implants into silicon. This results in higher activation and restricted diffusion of the B implants after annealing, and there are also significant differences in the microstructure after annealing compared with B implants into silicon. Rapid isothermal heating with an electron beam and furnace treatments are used to characterize the defect structure as a function of time and temperature. Defects are seen to influence the diffusion of non-substitutional boron.

THEORETICAL ROAD DAMAGE DUE TO DYNAMIC TYRE FORCES OF HEAVY VEHICLES. PART 2: SIMULATED DAMAGE CAUSED BY A TANDEM-AXLE VEHICLE.

The literature relating to road surface failure and design is briefly reviewed and the conventional methods for assessing the road damaging effects of dynamic tire forces are examined. A new time domain technique for analyzing dynamic tire forces and four associated road damage criteria are presented. The force criteria are used to examine the road damaging characteristics of a simple tandem-axle vehicle model for a range of speed and road roughness conditions. It is concluded that for the proposed criteria, the theoretical service life of road surfaces that are prone to fatigue failure may be reduced significantly by the dynamic component of wheel forces. The damage done to approximately five per cent of the road surface area during the passage of a theoretical model vehicle at typical highway speeds may be increased by as much as four times.

Defect and disorder reduction by annealing in hydrogenated tetrahedral amorphous carbon

Hydrogenated tetrahedral amorphous carbon (ta-C:H) is a form of diamond-like carbon with a high sp3 content (>60%), grown here using a plasma beam source. Information on the behaviour of hydrogen upon annealing is obtained from effusion measurements, which show that hydrogen does not effuse significantly at temperatures less than 500 °C in films grown using methane and 700 °C in films grown using acetylene. Raman measurements show no significant structural changes at temperatures up to 300 °C. At higher temperatures, corresponding to the onset of effusion, the Raman spectra show a clustering of the sp2 phase. The density of states of ta-C:H is directly measured using scanning tunnelling spectroscopy. The measured gradients of the conduction and valence band tails increase up to 300 °C, confirming the occurrence of band tail sharpening. Examination of the photoluminescence background in the Raman spectra shows an increase in photoluminescence intensity with decreasing defect density, providing evidence that paramagnetic defects are the dominant non-radiative recombination centres in ta-C:H.

Simulated superior performance of superjuction bipolar transistors

This paper presents for the first time an investigation and comparison of the superjunction IGBT (SJBT) as proposed in [1,2] and the current state of art Field Stop IGBT [3,4]. Simulation results indicate the superior performance of the superjunction IGBT under switching conditions. For the same conditions, at a collector current density of 100A/cm2 and on-state voltage 1.6 V the switching off losses for a SJBT and Field-Stop IGBT are 1 and 4.5 mJ/cm 2 respectively. © 2006 IEEE.