Supersonic laser deposition of Ti and Ti64 alloys

The importance of metal coating technologies drives the continuous improvement of metal deposition techniques for application in a wide range of industrial sectors. This work presents the foundations of a new process technology for the deposition of Ti and Ti64 coatings on various substrates using supersonic powder streams and impact site laser heating. Full density metallic deposits are obtained under appropriate impact conditions without the need for transiting the melting point of the deposited material or substrate leading to large energy savings. Details of the experimental approach will be presented along with the general characteristics of the titanium coatings produced using this novel coatings method.

Relaxation and fracture characteristics in Co-based amorphous alloys

In this article a study of the fracture characteristics of Co66Fe4Mo2Si16B12 amorphous ribbon in the as-quenched state and after relaxation is presented. In the as-quenched state, the morphology of the crack surface shows a 'vein pattern' structure that corresponds to a large amount of plastic flow. After relaxation the surface morphology of the crack shows that when the temperature of the thermal annealing increases the plastic flow involved in the crack decreases. In the as-quenched state dynamic fracture characteristics (crack branching and stress wave induced crack) have been observed. These dynamic characteristics have not been observed in the relaxed samples but in the samples annealed at 250 °C for 20 min apart from the main crack, a crack along the width of the ribbon has been observed. © 2006 Elsevier B.V. All rights reserved.

Plastic deformation of metals and alloys

This chapter focuses on relationships between plastic deformation structures and mechanical properties in metals and alloys deforming by dislocation glide. We start by summarizing plastic deformation processes, then look at the fundamental mechanisms of plastic deformation and explore how deformation structures evolve. We then turn to experimental techniques for characterization which have allowed deformation microstructures to be quantified in terms of common structural parameters. The microstructural evolution has been described over many length scales and analyzed theoretically based on general principles. The deformation microstructures are related to work hardening stages. Finally we identify correlations between a wide range of microstructural features and mechanical properties, particularly flow stress, and use experimental observations to illustrate their inter-relationships.

Light absorption and electrical transport in Si:O alloys for photovoltaics

Thin films (100-500 nm) of the Si:O alloy have been systematically characterized in the optical absorption and electrical transport behavior, by varying the Si content from 43 up to 100 at. %. Magnetron sputtering or plasma enhanced chemical vapor deposition have been used for the Si:O alloy deposition, followed by annealing up to 1250 °C. Boron implantation (30 keV, 3-30× 1014 B/cm2) on selected samples was performed to vary the electrical sheet resistance measured by the four-point collinear probe method. Transmittance and reflectance spectra have been extracted and combined to estimate the absorption spectra and the optical band gap, by means of the Tauc analysis. Raman spectroscopy was also employed to follow the amorphous-crystalline (a-c) transition of the Si domains contained in the Si:O films. The optical absorption and the electrical transport of Si:O films can be continuously and independently modulated by acting on different parameters. The light absorption increases (by one decade) with the Si content in the 43-100 at. % range, determining an optical band gap which can be continuously modulated into the 2.6-1.6 eV range, respectively. The a-c phase transition in Si:O films, causing a significant reduction in the absorption coefficient, occurs at increasing temperatures (from 600 to 1100 °C) as the Si content decreases. The electrical resistivity of Si:O films can be varied among five decades, being essentially dominated by the number of Si grains and by the doping. Si:O alloys with Si content in the 60-90 at. % range (named oxygen rich silicon films), are proved to join an appealing optical gap with a viable conductivity, being a good candidate for increasing the conversion efficiency of thin-film photovoltaic cell. © 2010 American Institute of Physics.

Thermal material with low curie temperature in a thermally actuated superconducting flux pump system

A thermally actuated flux pump is an efficient method to magnetize the high-temperature superconductor (HTS) bulk without applying a strong magnetic field. A thermal material is employed as a magnetic switch, which decides the efficiency of the system. To measure the Curie temperatures of those samples without destroying them, the nondestructive Curie temperature (NDT) measurement was developed. The Curie temperature of gadolinium (Gd) was measured by the NDT method and compared to the results from superconducting quantum interference device (SQUID). Because the SQUID tests require the sample to be cut into small piece, a constant shape of the testing sample could not be guaranteed. The demagnetizing effect was considered to remove the shape effect. The intrinsic permeability was modified from the apparent susceptibility by considering demagnetization. A thermal material with low Curie temperature, Mg 0.15Cu0.15Zn0.7Ti0.04Fe 1.96O4, was synthesized and its performance was tested and compared with previous thermal materials. Comparisons of three thermal materials, including the Curie temperature and the permeability, will be detailed in the paper. © 2002-2011 IEEE.