Crystal growth of melt-textured Nd-123 under 1% oxygen partial pressure atmosphere

Crystal growth of melt-textured Nd-123 pseudo-crystals was investigated via an isothermal solidification with top-seeding technique under a 1%O2 in N2 atmosphere. Non-steady state solidification was observed at low undercooling, in contrast to an almost linear growth at higher undercooling. Similar to processing in air, the substitution of Nd/Ba was found to decrease from the seed position to the edge of the crystal. In addition, the volume fraction of Nd-422 particles decreased in the solid as solidification proceeded. As a result of these microstructural inhomogeneities, the critical temperature and the critical current density varied within the crystal even for samples processed isothermally, despite the narrow solid solution range of the Nd-123 phase under a reduced pO2 atmosphere.

Magnetic field and current distributins in melt-textured YBa 2Cu 3O 7-x with an artificial grain boundary

Using a magneto-optical (MO) technique, magnetic field distributions have been measured in a melt-textured YBa 2Cu 3O 7-x bulk superconductor, joined to form an artificial grain boundary (GB), in an external magnetic field perpendicular to the sample surface. The magnetic field at a weak section of the GB shows different values between the field increasing up to 150mT and decreasing down to 0T after zero-field-cooling. Namely, the magnetic field in increasing field is higher than that in decreasing field, even in the same external field. This result supports a model in which such differences in magnetic field at the weak-link GB give rise to the hysteresis behavior in the field dependence of transport critical current density in polycrystalline samples. The field distributions across a well-joined region of the GB behave similarly to the adjoining bulk material and this result indicates the possibility of creating useful artifacts provided that the strongly coupled sections can be reproduced on a larger scale.

Behavior of bulk melt-textured YBCO single domains subjected to crossed magnetic fields

We have experimentally investigated the crossed magnetic field effects on bulk melt-processed YBCO single domains. The samples were first permanently magnetized along their c-axis and then subjected to several cycles of a transverse magnetic field parallel to the ab planes. The magnetic properties along the c and ab directions were simultaneously measured using a couple of orthogonal pick-up coils as well as a Hall probe placed against the sample surface. The effects of both sweep amplitude and polarity were investigated. Field sweeps of alternate polarities are shown to affect the decay of the c-axis magnetization much more strongly than field sweeps of unique polarity do. However, the c-axis magnetization does not show any saturation even after a large number of field sweeps. Next, a micro-Hall probe scanning system was used to measure the distribution of magnetic induction over the top surface of the single domain subjected to the same combination of magnetic fields. The results are shown to be consistent with those determined with the sensing coils and bring out the role played by geometric effects.

How is somatosensory information used to adapt to changes in the mechanical environment?

Recent studies examining adaptation to unexpected changes in the mechanical environment highlight the use of position error in the adaptation process. However, force information is also available. In this chapter, we examine adaptation processes in three separate studies where the mechanical environment was changed intermittently. We compare the expected consequences of using position error and force information in the changes to motor commands following a change in the mechanical environment. In general, our results support the use of position error over force information and are consistent with current computational models of motor learning. However, in situations where the change in the mechanical environment eliminates position error the central nervous system does not necessarily respond as would be predicted by these models. We suggest that it is necessary to take into account the statistics of prior experience to account for our observations. Another deficiency in these models is the absence of a mechanism for modulating limb mechanical impedance during adaptation. We propose a relatively simple computational model based on reflex responses to perturbations which is capable of accounting for iterative changes in temporal patterns of muscle co-activation.