ANNEALING BEHAVIOUR OF HIGH DOSE As** plus IMPLANTS.

The annealing behaviour of doses up to 4. 10**1**6 ions/cm**2 implanted at ion currents up to 10ma is described. Differences between rapid isothermal and furnace annealing in the measured sheet resistances are due to different amounts of diffusion and to loss of dopant by evaporation. Implantation at high currents (10ma) does not appear to affect the quality of the regrown material provided the temperature rise during implantation is small.

REGROWTH RATES OF AMORPHOUS LAYERS IN SILICON-ON-SAPPHIRE FILMS.

The rate and direction of regrowth of amorphous layers, created by self-implantation, in silicon-on-sapphire (SOS) have been studied using time resolved reflectivity (TRR) experiments performed simultaneously at two wavelengths. Regrowth of an amorphous layer towards the surface was observed in specimens implanted with 3 multiplied by (times) 10**1**5Si** plus /cm**2 at 50keV and regrowth of a buried amorphous layer, from a surface seed towards the sapphire, was observed in specimens implanted with 1 multiplied by (times) 10**1**5Si** plus /cm**2 at 175keV. Rapid isothermal heating to regrow the layers was performed in an electron beam annealing system. The combination of 514. 5nm and 632. 8nm wavelengths was found to be particularly useful for TRR studies since the high absorption in amorphous silicon, at the shorter wavelength, means that the TRR trace is not complicated by reflection from the silicon-sapphire interface until regrowth is nearly complete.

RESIDUAL DEFECTS FOLLOWING RAPID ANNEALING OF BORON IMPLANTED SILICON WITH AND WITHOUT PREAMORPHISATION BY SILICON IMPLANTATION.

Implants of boron into silicon which has been made amorphous by silicon implantation have a shallower depth profile than the same implants into silicon. This results in higher activation and restricted diffusion of the B implants after annealing, and there are also significant differences in the microstructure after annealing compared with B implants into silicon. Rapid isothermal heating with an electron beam and furnace treatments are used to characterize the defect structure as a function of time and temperature. Defects are seen to influence the diffusion of non-substitutional boron.

Crystal growth of melt-textured Nd-123 under 1% oxygen partial pressure atmosphere

Crystal growth of melt-textured Nd-123 pseudo-crystals was investigated via an isothermal solidification with top-seeding technique under a 1%O2 in N2 atmosphere. Non-steady state solidification was observed at low undercooling, in contrast to an almost linear growth at higher undercooling. Similar to processing in air, the substitution of Nd/Ba was found to decrease from the seed position to the edge of the crystal. In addition, the volume fraction of Nd-422 particles decreased in the solid as solidification proceeded. As a result of these microstructural inhomogeneities, the critical temperature and the critical current density varied within the crystal even for samples processed isothermally, despite the narrow solid solution range of the Nd-123 phase under a reduced pO2 atmosphere.

Contrasting code performances for computational aeroacoustics of jets

The numerical propagation of subcritical Tollmein-Schlichting (T-S), inviscid vortical and cut-on acoustic waves is explored. For the former case, the performances of the very different NEAT, NTS, HYDRA, FLUXp and OSMIS3D codes is studied. A modest/coarse hexahedral computational grid that starkly shows differences between the different codes and schemes used in them is employed. For the same order of discretization the five codes show similar results. The unstructured codes are found to propagate vortical and acoustic waves well on triangular cell meshes but not the T-S wave. The above code contrasting exercise is then carried out using implicit LES or Smagorinsky LES for and Ma = 0.9 plane jet on modest 0.5 million cell grids moving to circa 5 million cell grids. For this case, even on the coarse grid, for all codes results were generally encouraging. In general, the spread in computational results is less than the spread of the measurements. Interestingly, the finer grid turbulence intensity levels are slightly more under-predicted than those of the coarse grid. This difference is attributed to the numerical dispersion error having a favourable coarse grid influence. For a non-isothermal jet, HYDRA and NTS also give encouraging results. Peak turbulence values along the jet centreline are in better agreement with measurements than for the isothermal jets. Copyright © 2006 by University of Wales.

Design of carbon nanotubes based microwave applications employing mechanical resonance analysis

Carbon nanotubes (CNTs) have good mechanical properties and unique structural, electronic, thermal, and optical characteristics. In this work, we present the results of our investigations of a resonator device based on embedded vertical CNT arrays. The device's design is based on the mechanical resonance of the tubes. CoventorWare FEA tools have been used to simulate the mechanical resonance frequencies of the vertical nanotubes arrays integrated on a silicon substrate. ©2008 IEEE.

Carbon nanotube based cathodes for microwave amplifiers

We have studied two different kinds of electron tubes using a cold field emission cathode as the electron source. This cathode is an array of vertically aligned multiwall carbon nanotubes. The first device is a triode. With this device, we demonstrated the modulation at 32 GHZ of a 1.4 A/cm2 peak current density with a 82% modulation ratio. The second device is a traveling wave tube. For this device, the objective is to test a cathode delivering a 2 A/cm 2 electron beam. ©2009 IEEE.

Improved infrared thermal imaging of a CMOS MEMS device

We report a technique which can be used to improve the accuracy of infrared (IR) surface temperature measurements made on MEMS (Micro-Electro-Mechanical- Systems) devices. The technique was used to thermally characterize a SOI (Silicon-On-Insulator) CMOS (Complementary Metal Oxide Semiconductor) MEMS thermal flow sensor. Conventional IR temperature measurements made on the sensor were shown to give significant surface temperature errors, due to the optical transparency of the SiO 2 membrane layers and low emissivity/high reflectivity of the metal. By making IR measurements on radiative carbon micro-particles placed in isothermal contact with the device, the accuracy of the surface temperature measurement was significantly improved. © 2010 EDA Publishing/THERMINIC.

CFD-DEM simulation of propagation of sound waves in fluid particles fluidised medium

In this work, speed of sound in 2 phase mixture has been explored using CFD-DEM (Computational Fluid Dynamcis - Discrete Element Modelling). In this method volume averaged Navier Stokes, continuity and energy equations are solved for fluid. Particles are simulated as individual entities; their behaviour is captured by Newton's laws of motion and classical contact mechanics. Particle-fluid interaction is captured using drag laws given in literature.The speed of sound in a medium depends on physical properties. It has been found experimentally that speed of sound drops significantly in 2 phase mixture of fluidised particles because of its increased density relative to gas while maintaining its compressibility. Due to the high rate of heat transfer within 2 phase medium as given in Roy et al. (1990), it has been assumed that the fluidised gas-particle medium is isothermal.The similar phenomenon has been tried to be captured using CFD-DEM numerical simulation. The disturbance is introduced and fundamental frequency in the medium is noted to measure the speed of sound for e.g. organ pipe. It has been found that speed of sound is in agreement with the relationship given in Roy et al. (1990). Their assumption that the system is isothermal also appears to be valid.

Collapse mechanism maps for the hollow pyramidal core of a sandwich panel under transverse shear

The finite element method has been used to develop collapse mechanism maps for the shear response of sandwich panels with a stainless steel core comprising hollow struts. The core topology comprises either vertical tubes or inclined tubes in a pyramidal arrangement. The dependence of the elastic and plastic buckling modes upon core geometry is determined, and optimal geometric designs are obtained as a function of core density. For the hollow pyramidal core, strength depends primarily upon the relative density ρ̄ of the core with a weak dependence upon tube slenderness. At ρ̄ below about 3%, the tubes of the pyramidal core buckle plastically and the peak shear strength scales linearly with ρ̄. In contrast, at ρ̄ above 3%, the tubes do not buckle and a stable shear response is observed. The predictions of the current study are in excellent agreement with previous measurements on the shear strength of the hollow pyramidal core, and suggest that this core topology is attractive from the perspectives of both core strength and energy absorption. © 2011 Elsevier Ltd. All rights reserved.

Improved jet noise modeling using a new time-scale.

To calculate the noise emanating from a turbulent flow using an acoustic analogy knowledge concerning the unsteady characteristics of the turbulence is required. Specifically, the form of the turbulent correlation tensor together with various time and length-scales are needed. However, if a Reynolds Averaged Navier-Stores calculation is used as the starting point then one can only obtain steady characteristics of the flow and it is necessary to model the unsteady behavior in some way. While there has been considerable attention given to the correct way to model the form of the correlation tensor less attention has been given to the underlying physics that dictate the proper choice of time-scale. In this paper the authors recognize that there are several time dependent processes occurring within a turbulent flow and propose a new way of obtaining the time-scale. Isothermal single-stream flow jets with Mach numbers 0.75 and 0.90 have been chosen for the present study. The Mani-Gliebe-Balsa-Khavaran method has been used for prediction of noise at different angles, and there is good agreement between the noise predictions and observations. Furthermore, the new time-scale has an inherent frequency dependency that arises naturally from the underlying physics, thus avoiding supplementary mathematical enhancements needed in previous modeling.

The nonlinear heat release response of stratified lean-premixed flames to acoustic velocity oscillations

This paper analyzes the forced response of swirl-stabilized lean-premixed flames to high-amplitude acoustic forcing in a laboratory-scale stratified burner operated with CH4 and air at atmospheric pressure. The double-swirler, double-channel annular burner was specially designed to generate high-amplitude acoustic velocity oscillations and a radial equivalence ratio gradient at the inlet of the combustion chamber. Temporal oscillations of equivalence ratio along the axial direction are dissipated over a long distance, and therefore the effects of time-varying fuel/air ratio on the response are not considered in the present investigation. Simultaneous measurements of inlet velocity and heat release rate oscillations were made using a constant temperature anemometer and photomultiplier tubes with narrow-band OH*/CH* interference filters. Time-averaged and phase-synchronized CH* chemiluminescence intensities were measured using an intensified CCD camera. The measurements show that flame stabilization mechanisms vary depending on equivalence ratio gradients for a constant global equivalence ratio (φg=0.60). Under uniformly premixed conditions, an enveloped M-shaped flame is observed. In contrast, under stratified conditions, a dihedral V-flame and a toroidal detached flame develop in the outer stream and inner stream fuel enrichment cases, respectively. The modification of the stabilization mechanism has a significant impact on the nonlinear response of stratified flames to high-amplitude acoustic forcing (u'/U∼0.45 and f=60, 160Hz). Outer stream enrichment tends to improve the flame's stiffness with respect to incident acoustic/vortical disturbances, whereas inner stream stratification tends to enhance the nonlinear flame dynamics, as manifested by the complex interaction between the swirl flame and large-scale coherent vortices with different length scales and shedding points. It was found that the behavior of the measured flame describing functions (FDF), which depend on radial fuel stratification, are well correlated with previous measurements of the intensity of self-excited combustion instabilities in the stratified swirl burner. The results presented in this paper provide insight into the impact of nonuniform reactant stoichiometry on combustion instabilities, its effect on flame location and the interaction with unsteady flow structures. © 2011 The Combustion Institute.

Hardfacing using supersonic laser depostion of stellite-6

The capability of manufacturing coatings is of central importance in engineering design. Many components require nowadays the application of additional layers, to enhance mechanical properties and protect against hostile environments. Supersonic Laser Deposition (SLD) is a novel coating method, based upon Cold Spray (CS) principles. In this technique the deposition velocities can be significantly lower than those required for effective bonding in CS applications. The addition of laser heat energy permits a change in the thermodynamic experience of impacting particles, thereby offering a greater opportunity for metallurgical bonding at lower velocities compared to the CS process technology. The work reported in this paper demonstrates the ability of the SLD process to deliver hard facing materials to engineering surfaces. Stellite-6 has been deposited on low carbon steel tubes over a range of process parameters, determining the appropriate target power and traverse speeds for coating deposition. Coating properties and parameters were examined to determine the main properties, micro-structure and processing cost. Their morphology was studied through optical microscopy, SEM and X-Ray Diffraction. The results have shown that SLD is capable of depositing Stellite-6, with enhanced properties compared to laser clad counterparts.

TRANSIENT SCANNING ELECTRON BEAM ANNEALING METHODS USED TO STUDY DIFFUSION AND DEFECTS IN IMPLANTED SILICON.

Rapid thermal annealing of arsenic and boron difluoride implants, such as those used for source/drain regions in CMOS, has been carried out using a scanning electron beam annealer, as part of a study of transient diffusion effects. Three types of e-beam anneal have been performed, with peak temperatures in the range 900 -1200 degree C; the normal isothermal e-beam anneals, together with sub-second fast anneals and 'dual-pulse' anneals, in which the sample undergoes an isothermal pre-anneal followed by rapid heating to the required anneal temperature is less than 0. 5s. The diffusion occuring during these anneal cycles has been modelled using SPS-1D, an implant and diffusion modelling program developed by one of the authors. This has been modified to incorporate simulated temperature vs. time cycles for the anneals. Results are presented applying the usual equilibrium clustering model, a transient point-defect enhancement to the diffusivity proposed recently by Fair and a new dynamic clustering model for arsenic. Good agreement with SIMS measurements is obtained using the dynamic clustering model, without recourse to a transient defect model.