Defined etching of carbon-diamond films on silicon using an oxygen plasma with titanium masking

A technique for pattern transfer onto carbon-diamond films deposited by radio-frequency plasma-enhanced chemical vapour deposition is reported. Such a technique involves standard photolithography processes and reactive ion etching by oxygen and is compatible with present day microelectronic technology. The patterns transferred are well defined with very good resolution. © 1992.

Performance of CMOS Devices in Silicon-on-Sapphire Films After Solid-Phase Epitaxial Growth With Rapid Electron-Beam Heating

The crystal quality of 0.3-μm-thick as-grown epitaxial silicon-on-sapphire (SOS) was improved using solid-phase epitaxy (SPE) by implantation with silicon to 1015 ions/cm2 at 175 keV and rapid annealing using electron-beam heating, n-channel and p-channel transistormobilities increased by 31 and 19 percent, respectively, and a reduction in ring-oscillator stage delay confirmed that crystal defects near the upper silicon surface had been removed. Leakage in n-channel transistors was not significantly affected by the regrowth process but for p-channel transistors back-channel leakage was considerably greater than for the control devices. This is attributed to aluminum released by damage to the sapphire during silicon implantation. © 1985 IEEE

REGROWTH RATES OF AMORPHOUS LAYERS IN SILICON-ON-SAPPHIRE FILMS.

The rate and direction of regrowth of amorphous layers, created by self-implantation, in silicon-on-sapphire (SOS) have been studied using time resolved reflectivity (TRR) experiments performed simultaneously at two wavelengths. Regrowth of an amorphous layer towards the surface was observed in specimens implanted with 3 multiplied by (times) 10**1**5Si** plus /cm**2 at 50keV and regrowth of a buried amorphous layer, from a surface seed towards the sapphire, was observed in specimens implanted with 1 multiplied by (times) 10**1**5Si** plus /cm**2 at 175keV. Rapid isothermal heating to regrow the layers was performed in an electron beam annealing system. The combination of 514. 5nm and 632. 8nm wavelengths was found to be particularly useful for TRR studies since the high absorption in amorphous silicon, at the shorter wavelength, means that the TRR trace is not complicated by reflection from the silicon-sapphire interface until regrowth is nearly complete.

PHOTOENHANCED DEPOSITION OF HYDROGENATED AMORPHOUS SILICON THIN FILMS.

This paper will review the different U. V. lamp photo-CVD (Chemical Vapor Deposition) techniques which have been utilized for the production of highly photoconductive hydrogenated amorphous silicon (a-Si:H) thin films. Most of these require the transmission of U. V. light through a window into the reaction vessel; leading to unwanted U. V. light absorption by the window and the a-Si:H film which tends to form on its inner surface. A deposition system developed in our laboratory will also be described, which circumvents these problems by incorporating a windowless discharge lamp into the reaction vessel.