Test on prestressed concrete beam with AFRP spiral confinement and external aramid tendons

This paper describes an experimental study of a new form of prestressed concrete beam. Aramid Fiber Reinforced Polymers (AFRPs) are used to provide compression confinement in the form of interlocking circular spirals, while external tendons are made from parallel-lay aramid ropes. The response shows that the confinement of the compression flange significantly increases the ductility of the beam, allowing much better utilization of the fiber strength. The failure of the beam is characterized by rupture of spiral confinement reinforcement.

Behavior of RC beams retrofitted with CARDIFRC after thermal cycling

This study investigates the effect of thermal cycling on the performance of concrete beams retrofitted with CARDIFRC, a new class of high performance fiber-reinforced cement-based material that is compatible with concrete. Twenty four beams were subjected to 24 h thermal cycles between 25 and 90°C. One third of the beams were reinforced either in flexure only or in flexure and shear with conventional steel reinforcement and used as control specimens. The remaining sixteen beams were retrofitted with CARDIFRC strips to provide external flexural and/or shear strengthening. All beams were exposed to a varied number of 24 h thermal cycles ranging from 0 to 90 and were tested in four-point bending at room temperature. The tests indicated that the retrofitted members were stronger and stiffer than control beams, and more importantly, that their failure initiated in flexure without any signs of interfacial delamination cracking. The results of these tests are presented and compared to analytical predictions. The predictions show good correlation with the experimental results. © 2010 ASCE.

Residual strength of GRP laminates with multiple randomly distributed fragment impacts

The residual tensile strength of glass fibre reinforced composites with randomly distributed holes and fragment impact damages have been investigated. Experiments have been performed on large scale panels and small scale specimens. A finite element model has been developed to predict the strength of multi-axial panels with randomly distributed holes. Further, an effective analytical model has been developed using percolation theory. The model gives an estimation of the residual strength as function of removed surface area caused by the holes. It is found that if 8% of the area is removed, the residual strength is approximately 50% of the un-damaged strength. © 2014 Published by Elsevier Ltd.

A microstructural investigation of deformation in fine SiC particulate- and whisker-reinforced aluminium-matrix composites

Aluminium-based composites, reinforced with low volume fractions of whiskers and small particles, have been formed by a powder route. The materials have been tested in tension, and the microstructures examined using transmission electron microscopy. The whisker composites showed an improvement in flow stress over the particulate composites, and this was linked to an initially enhanced work-hardening rate in the whisker composites. The overall dislocation densities were estimated to be somewhat higher in the whisker composites than the particulate composites, but in the early stages of deformation the distribution was rather different, with deformation in the whisker material being far more localized and inhomogeneous. This factor, together with differences in the internal stress distribution in the materials, is used to explain the difference in mechanical properties.

The fracture energy of metal fibre reinforced ceramic composites (MFCs)

A model is presented for prediction of the fracture energy of ceramic-matrix composites containing dispersed metallic fibres. It is assumed that the work of fracture comes entirely from pull-out and/or plastic deformation of fibres bridging the crack plane. Comparisons are presented between these predictions and experimental measurements made on a commercially-available composite material of this type, containing stainless steel (304) fibres in a matrix predominantly comprising alumina and alumino-silicate phases. Good agreement is observed, and it's noted that there is scope for the fracture energy levels to be high (~20kJm-2). Higher toughness levels are both predicted and observed for coarser fibres, up to a practical limit for the fibre diameter of the order of 0.5mm. Other deductions are also made concerning strategies for optimisation of the toughness of this type of material. © 2010 Elsevier Ltd.