Effect of deposition conditions on the chemical bonding in sputtered carbon nitride films

A balanced planar r.f. powered magnetron sputter source has been used to deposit carbon nitride films from a graphite target under various conditions. Sample temperature, bias voltage and nitrogen content in the gas mixture were varied. The effects of oxygen, methane and ammonia on the film growth were also studied. Special attention was paid to the effects of the deposition parameters on the structure of the films, in particular the hybridisation of the carbon and nitrogen bonding. The chemical bonding of the carbon and nitrogen atoms was studied by electron energy loss spectroscopy (EELS). The chemical composition was evaluated by Rutherford back-scattering. The intensity of transitions to π antibonding orbitals, as revealed by EELS, was found to increase with the nitrogen content in the films. Ion bombardment of the films during growth and the addition of oxygen or hydrogen-rich gases further increased the proportion of π bonds of both the carbon and nitrogen atoms. It is suggested that the increase in the transitions to μ antibond orbitals is to be explained by increased sp2 or possibly sp hybridisation of the carbon and nitrogen. Also, the effect of annealing on the bonding of nitrogen rich films after deposition was tested. The changes caused by nitrogen and deposition conditions are consistent with previous reports on the formation of paracyanogen structures.

Hydrogenated amorphous silicon and silicon nitride deposited at less than 100° C by ECR-PECVD for thin film transistors

A systematic study has been made of the growth of both hydrogenated amorphous silicon (a-Si:H) and silicon nitride (a-SiN) by electron cyclotron resonance plasma enhanced chemical vapour deposition (ECR-PECVD). In the case of a-SiN, helium and nitrogen gas is injected into the system such that it passes through the resonance zone. These highly ionised gases provide sufficient energy to ionise the silane gas, which is injected further downstream. It is demonstrated that a gas phase reaction occurs between the silane and nitrogen species. It is control of the ratio of silane to nitrogen in the plasma which is critical for the production of stoichiometric a-SiN. Material has been produced at 80°C with a Si:N ratio of 1:1.3 a breakdown strength of ∼6 MV cm-1 and resistivity of > 1014 Ω cm. In the case of a-Si:H, helium and hydrogen gas is injected into the ECR zone and silane is injected downstream. It is shown that control of the gas phase reactions is critical in this process also. a-Si:H has been deposited at 80 °C with a dark conductivity of 10-11 Ω-1 cm-1 and a photosensitivity of justbelowl 4×104. Such materials are suitable for use in thin film transistors on plastic substrates.