EFFECT OF GRAIN-BOUNDARY MICROSTRUCTURE ON CAVITY NUCLEATION IN A NICKEL-BASED SUPERALLOY.

A study is presented of grain-boundary cavitation produced in Nimonic 80A by cold-deformation and stress-free annealing. The cavities were found to originate either from transverse cracking of carbide particles, or from decohesion of the particle-grain boundary interfaces. This decohesion could occur either during deformation, or during annealing. The cavities were invariably located at or close to the point of impingement of a matrix slip band on the grain boundary, but not all slip bands at a particular boundary were associated with cavitation. Quantitative evidence is presented showing that the mean number of dislocations associated with each slip band increases with macroscopic strain, but there is considerable variation between slip bands. This accounts for the differential ability of slip bands to result in cavity nucleation.

INFLUENCE OF ATMOSPHERIC HUMIDITY ON THE ABRASIVE WEAR OF METALS.

A pin-on-disc apparatus has been used to obtain continuous simultaneous measurements of the wear and friction (sliding force) behaviour of metals on bonded silicon carbide abrasive paper under conditions of controlled humidity. Iron, mild steel, and copper exhibit qualitatively similar wear behaviour; the wear rate decreases progressively with the number of passes over the same track. In contrast, the wear rate of titanium remains constant. Variation in atmospheric humidity has little effect on the wear rates of copper or titanium, although a slight effect was found in mild steel and iron. Refs.