Intergranular and intragranular properties of superconducting multifilamentary Bi 2223 Ag tapes : comparison of electrical transport and magnetic measurement methods

Several experimental techniques have been used in order to characterize the properties of multifilamentary Bi-2223 / Ag tapes. Pristine samples were investigated by electrical resistivity, current-voltage characteristics and DC magnetic moment measurements. Much emphasis is placed on comparing transport (direct) and magnetic (indirect) methods for determining the critical current density as well as the irreversibility line and resolving usual lacks of consistency due to the difference in measurement techniques and data analysis. The effect of an applied magnetic field, with various strengths and directions, is also studied and discussed. Next, the same combination of experiments was performed on bent tapes in order to bring out relevant information regarding the intergranular coupling. A modified Brandt model taking into account different types of defects within the superconducting filaments is proposed to reconciliate magnetic and transport data.

YBa 2Cu 3O 7-δ thick films on Ag prepared by the Electrophoretic Deposition technique

YBa 2Cu 3O 7-δ thick films have been deposited onto Ag substrates by the Electrophoretic Deposition (EPD) technique. Different microstructures and electrical behaviours were observed depending on the starting powder. Coatings prepared from commercial powder displayed significant porosity and the superconducting transition width was found to be magnetic-field dependent. Films produced from home-made coprecipitated powder are denser but contain some secondary phases. No dependence of the resistive transition as a function of magnetic field (H 20 Oe) was observed in that case. © 2006 IOP Publishing Ltd.

Intragranular and intergranular behaviour of multifilamentary Bi-2223/Ag tapes

This communication aims at reporting the superconducting properties of Bi-2223/Ag tapes determined by using various measuring techniques. First, the original samples have been characterized by electrical resistance, AC susceptibility, and DC magnetization. The transport (intergranular) critical current vs. magnetic field was also determined at T = 77 K using pulsed currents up to 40 A. Next, the same combination of experiments was performed on bent tapes in order to bring out relevant information concerning the strength of the intergranular coupling. The results show that intergranular and intragranular currents differ by at least one order of magnitude. Finally, additional magnetic measurements were carried out in order to determine the anisotropy ratio Jc ab/Jc c, which was found to lie around 30. © 2002 Elsevier Science B.V. All rights reserved.