This paper describes the design considerations for a proposed aerodynamic characterization facility (ACF) for micro aerial vehicles (MAVs). This is a collaborative effort between the Air Force Research Laboratory Munitions Directorate (AFRL/MN) and the University of Florida Research and Engineering Education Facility (UF/REEF). The ACF is expected to provide a capability for the characterization of the aerodynamic performance of future MAVs. This includes the ability to gather the data necessary to devise control strategies as well as the potential to investigate aerodynamic 'problem areas' or specific failings. Since it is likely that future MAVs will incorporate advanced control strategies, the facility must enable researchers to critically assess such novel methods. Furthermore, the aerodynamic issues should not be seen (and tested) in isolation, but rather the facility should be able to also provide information on structural responses (such as aeroelasticity) as well as integration issues (say, thrust integration or sensor integration). Therefore the mission for the proposed facility ranges form fairly basic investigations of individual technical issues encountered by MAVs (for example an evaluation of wing shapes or control effectiveness) all the way to testing a fully integrated vehicle in a flight configuration for performance evaluation throughout the mission envelope.

Thermal shock resistance of air plasma sprayed thermal barrier coatings

The spallation resistance of an air plasma sprayed (APS) thermal barrier coating (TBC) to cool-down/reheat is evaluated for a pre-existing delamination crack. The delamination emanates from a vertical crack through the coating and resides at the interface between coating and underlying thermally grown oxide layer (TGO). The coating progressively sinters during engine operation, and this leads to a depth-dependent increase in modulus. Following high temperature exposure, the coating is subjected to a cooling/reheating cycle representative of engine shut-down and start-up. The interfacial stress intensity factors are calculated for the delamination crack over this thermal cycle and are compared with the mode-dependent fracture toughness of the interface between sintered APS and TGO. The study reveals the role played by microstructural evolution during sintering in dictating the spallation life of the thermal barrier coating, and also describes a test method for the measurement of delamination toughness of a thin coating. © 2014 Elsevier Ltd.