Mechanisms of erosion of unfilled elastomers by solid particle impact

The mechanisms of material removal were studied during the erosion of two unfilled elastomers (natural rubber and epoxidised natural rubber). The effects of impact velocity and of lubrication by silicone oil were investigated. The development of surface features due to single impacts and during the early stages of erosion was followed by scanning electron microscopy. The basic material removal mechanism at impact angles of both 30° and 90° involves the formation and growth of fine fatigue cracks under the tensile surface stresses caused by impact. No damage was observed after single impacts; it was found that many successive impacts are necessary for material removal. It was found that the erosion rate has a very strong dependance on impact velocity above about 50 ms-1.

Solid particle erosion of boronized steels

Boronizing is a thermochemical diffusion-based process for producing iron boride layers in the surface of steel components. The boride layer is wear resistant and is very hard. Large residual stresses are found to exist in the surface layers, which are a function of substrate steel composition and heat treatment. By slow cooling from the boronizing temperature (900°C), a large compressive stress is developed in the boride layer. Hardening the steel by rapid cooling, either directly from the boronizing treatment or after subsequent austenitizing, develops tension in the coating which causes it to fracture. Tempering of the martensite produces compression in the coating, closing but not welding the cracks. The results of solid particle erosion experiments using silicon carbide, quartz, and glass bead erodents on boronized steels are presented.

Influence of particle properties on the erosive wear of sintered boron carbide

Sintered boron carbide is very hard, and can be an attractive material for wear-resistant components in critical applications. Previous studies of the erosion of less hard ceramics have shown that their wear resistance depends on the nature of the abrasive particles. Erosion tests were performed on a sintered boron carbide ceramic with silica, alumina and silicon carbide erodents. The different erodents caused different mechanisms of erosion, either by lateral cracking or small-scale chipping; the relative values of the hardness of the erodent and the target governed the operative mechanism. The small-scale chipping mechanism led to erosion rates typically an order of magnitude lower than the lateral fracture mechanism. The velocity exponents for erosion in the systems tested were similar to those seen in other work, except that measured with the 125 to 150 μm silica erodent. With this erodent the exponent was initially high, then decreased sharply with increasing velocity and became negative. It was proposed that this was due to deformation and fragmentation of the erodent particles. In the erosion testing of ceramics, the operative erosion mechanism is important. Care must be taken to ensure that the same mechanism is observed in laboratory testing as that which would be seen under service conditions, where the most common erodent is silica.

Failure mechanisms and toughness of Al2O3 ductile-particle toughened ceramics and SiC fibre-ceramic composites

The development of high performance ceramics and ceramic composites often relies on assumptions about their behaviour during loading and at failure. A crucial influence on the mechanical properties of these materials is the degree of sub-critical cracking, which post mortem investigations cannot adequately reveal. Hence a clear picture of the dynamic micromechanisms of cracking is required if applications of fracture and damage mechanics to theoretical models is to be meaningful.

A model for the erosive wear of rubber at oblique impact angles

A model has been developed to predict the erosive wear behaviour of elastomers under conditions of glancing impact by small hard particles. Previous work has shown the erosive wear mechanism of elastomers under these conditions to be similar in nature to that of abrasive wear by a sharp blade. The model presented here was developed from the model of Southern and Thomas for sliding abrasion, by combining their treatment of the growth of surface cracks with a model for particle impact in which the force - displacement relationship for an idealized flat-ended punch on a semi-infinite elastic solid was assumed. In this way an expression for the erosive wear rate was developed, and compared with experimental measurements of wear rate for natural rubber, styrene - butadiene rubber and a highly crosslinked polybutadiene rubber. Good qualitative agreement was found between the predictions of the model and the experimental measurements. The variation of erosion rate with impact velocity, impact angle, particle size, elastic modulus of the material, coefficient of friction and fatigue properties were all well accounted for. Quantitative agreement was less good, and the effects of erosive particle shape could not be accounted for. The reasons for these discrepancies are discussed. © 1992 IOP Publishing Ltd.

The generation of wear surfaces

Abrasive wear is likely to occur whenever a hard asperity or a trapped hard particle is dragged across a softer surface, and it has been estimated that this form of wear contributes to as many as half of the wear problems that are met in industry. Such damaging hard particles may be external contaminants, products of corrosion or even the debris from previous wear events. During the life of a component, damage caused by individual asperity or particle interactions builds up and, at each stage of its life, the worn surface is the result of many such superimposed wear events. The practical, quantitative prediction of wear rates depends on having both a satisfactory understanding of individual interactions and a suitable procedure for combining these when subsequent contacts are made on a surface whose topography and material properties may have been much changed Irom their initial states. The paper includes some details of an analytical model for the interaction of a representative asperity and the worn surface which can both predict the frictional force and the balance between ploughing, when material is displaced but not lost from the surface, and micromachining or cutting, when actual detachment occurs. Experiments tö !rvvéSuQ8Î8 the validity of the model have been carried out on a novel wear rig which provides very precise control over the position of the asperity and the counterface. This facility, together with that of on-board profilometry, means that it is possible to carry out wear experiments on areas of the surface whose previous deformation history is well known; in this way it is possible to follow the development of a worn surface in a controlled manner as the damage from individual wear events accumulates. Experimental data on the development of such a surface, produced by repeated parallel abrasion, are compared with the predictions of the model. © 1992 IOP Publishing Ltd.

Wear of hardfacing white cast irons by solid particle erosion

The response of three commercial weld-hardfacing alloys to erosive wear has been studied. These were high chromium white cast irons, deposited by an open-arc welding process, widely used in the mineral processing and steelmaking industries for wear protection. Erosion tests were carried out with quartz sand, silicon carbide grit and blast furnace sinter of two different sizes, at a velocity of 40 m s-1 and at impact angles in the range 20° to 90°. A monolithic white cast iron and mild steel were also tested for comparison. Little differences were found in the wear rates when silica sand or silicon carbide grit was used as the erodent. Significant differences were found, however, in the rankings of the materials. Susceptibility to fracture of the carbide particles in the white cast irons played an important role in the behaviour of the white cast irons. Sinter particles were unable to cause gross fracture of the carbides and so those materials with a high volume fraction of carbides showed the greatest resistance to erosive wear. Silica and silicon carbide were capable of causing fracture of the primary carbides. Concentration of plastic strain in the matrix then led to a high wear rate for the matrix. At normal impact with silica or silicon carbide erodents mild steel showed a greater resistance to erosive wear than these alloys. © 1995.