Impact of high-k dielectrics on breakdown performances of SiC and diamond Schottky diodes

This paper presents a comparison between SiC and diamond Schottky barrier diodes using the oxide ramp termination. The influences of the dielectric thickness and relative permittivity on the diode's electrical performance are investigated. Typical commercial drift layer parameters are used for this study. The extension of the space charge area throughout the drift region and the current distribution at breakdown are shown. The efficiency of the termination is also evaluated for both SiC and diamond diodes. © (2009) Trans Tech Publications, Switzerland.

Single crystal diamond schottky diodes - Practical design considerations for enhanced device performance

Novel alternatives to the conventional single crystal diamond Schottky metal-intrinsic-p+ (m-i-p+) diode is presented in this work. The conduction mechanism of the device is analysed and structural modifications to enhance its performance are proposed. The periodic inclusion of highly p+ doped thin δ-layers and p+ spots in the intrinsic voltage blocking layer of the diode drastically improves the forward performance of these devices enhancing the forward current of the device by a factor of 10 - 17 with a maximum forward current density of ̃ 40 A/cm 2 for a 2 kV device.

Fabrication of diamond based schottky barrier diodes with oxide ramp termination

The paper's goal is the first demonstration of the fabrication of high power Schottky diodes on synthetic diamond using oxide ramp termination. In order to allow full activated impurities at room temperature and a high hole mobility a low boron doping of the drift layer is employed. Several aspects of the manufacturing technology are presented. A termination with a small ramp angle can be obtained using only RIE technique due to diamond wafer nonuniformity (roughness). Experimental forward and reverse characteristics measured on diamond diodes are also included. © 2007 IEEE.

Smooth thin film C/diamond membranes with controllable optical band gaps

Mixed phase carbon-diamond films which consist of small grain diamond in an a:C matrix were deposited on polished Si using a radio frequency CH4 Ar plasma CVD deposition process. Ellipsometry, surface profilometry, scanning electron microscopy (SEM) and spectrophotometry were used to analyse these films. Film thicknesses were typically 50-100 nm with a surface roughness of ± 30 A ̊ over centimetre length scans. SEM analysis showed the films were smooth and pinhole free. The Si substrate was etched using backside masking and a directional etch to give taut carbon-diamond membranes on a Si grid. Spectrophotometry was used to analyse the optical properties of these membranes. Band gap control was achieved by varying the dc bias of the deposition process. Band gaps of 1.2 eV to 4.0 eV were achieved in these membranes. A technique for controlling the compressive stress in the films, which can range from 0.02 to 7.5 GPa has been employed. This has allowed the fabrication of thin, low stress, high band gap membranes that are extremely tough and chemically inert. Such carbon-diamond membranes seem promising for applications as windows in analytical instruments. © 1992.